Abstract:This research explores the behavior of Co40Fe40W10B10 when it is sputtered onto Si(100) substrates with a thickness (tf) ranging from 10 nm to 100 nm, and then altered by an annealing process at temperatures of 200 °C, 250 °C, 300 °C, and 350 °C, respectively. The crystal structure and grain size of Co40Fe40W10B10 films with different thicknesses and annealing temperatures are observed and estimated by an X-ray diffractometer pattern (XRD) and full-width at half maximum (FWHM). The XRD of annealing Co40Fe40W10B10 films at 200 °C exhibited an amorphous status due to insufficient heating drive force. Moreover, the thicknesses and annealing temperatures of body-centered cubic (BCC) CoFe (110) peaks were detected when annealing at 250 °C with thicknesses ranging from 80 nm to 100 nm, annealing at 300 °C with thicknesses ranging from 50 nm to 100 nm, and annealing at 350 °C with thicknesses ranging from 10 nm to 100 nm. The FWHM of CoFe (110) decreased and the grain size increased when the thickness and annealing temperature increased. The CoFe (110) peak revealed magnetocrystalline anisotropy, which was related to strong low-frequency alternative-current magnetic susceptibility (χac) and induced an increasing trend in saturation magnetization (Ms) as the thickness and annealing temperature increased. The contact angles of all Co40Fe40W10B10 films were less than 90°, indicating the hydrophilic nature of Co40Fe40W10B10 films. Furthermore, the surface energy of Co40Fe40W10B10 presented an increased trend as the thickness and annealing temperature increased. According to the results, the optimal conditions are a thickness of 100 nm and an annealing temperature of 350 °C, owing to high χac, large Ms, and strong adhesion; this indicates that annealing Co40Fe40W10B10 at 350 °C and with a thickness of 100 nm exhibits good thermal stability and can become a free or pinned layer in a magnetic tunneling junction (MTJ) application.

Surface Anisotropy Characterization and Microstructure of Cu–W Thin Films at Different Annealing Temperatures

ANISOTROPY BEHAVIOR OF SURFACE MORPHOLOGY AND PHASE STRUCTURE OF Cu-W THIN FILMS

Surface Morphology Anisotropy and Stress Distribution Uniformity in Annealed Cu–W Films

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Crystalline Orientation and Surface Structure Anisotropy of Annealed Thin Tungsten Films

Phase Structure and Residual Stress in Annealed Cu-W Films

The Surface Mapping and Crystal Orientation of Body-Centered Cubic Thin Metal Tungsten Films of Different Thickness

Morphological Characterization and Nanoindentation Hardness Scatter Evaluation for Cu-W Thin Films Based on Wavelet Transform

Morphological characterization of Cu-W thin films based on wavelet transform

Annealing Effect on the Contact Angle, Surface Energy, Electric Property, and Nanomechanical Characteristics of Co40Fe40W20 Thin Films

Molecular dynamics investigation of deposition and annealing behaviors of Cu atoms onto Cu(001) substrate

Molecular dynamics investigation of deposition and annealing behaviors of Cu atoms onto Cu(0 0 1) substrate

Effects of Periods on the Evolution of Microstructure and Mechanical Properties of Multilayered Cu-W Films During Thermal Annealing

Impact of Annealing on Magnetic Properties and Structure of Co40Fe40W20 Thin Films on Si(100) Substrate

Influence of annealing on microstructure and electrochromic properties of WO3 thin film

Investigation on the Interfacial Stability of Multilayered Cu–W Films at Elevated Deposition Temperatures During Co-Sputtering

Influence of Post-Annealing Treatment on the Morphology of Au Films Deposited on Liquid Surfaces

Influence of Thermal Annealing on the Morphology and Magnetic Domain Structure of Co Thin Films

Annealing Effect on the Characteristics of Co40Fe40W10B10 Thin Films on Si(100) Substrate

On the Evolution of Nano-Structures at the Al–Cu Interface and the Influence of Annealing Temperature on the Interfacial Strength

Heterogeneous Morphologies and Hardness of Co-Sputtered Thin Films of Concentrated Cu-Mo-W Alloys