Abstract:Carbon fiber reinforced silicon carbide matrix composites (C/SiC) have emerged as key materials for thermal protection systems owing to their high strength-to-weight ratio, high-temperature durability, resistance to oxidation, and outstanding reliability. However, manufacturing defects deteriorate the mechanical response of these composites under extreme thermal-force coupling conditions, prompting significant research attention. This study demonstrates a customized in situ loading device compatible with synchrotron radiation facilities, enabling high spatial and temporal resolution recording of internal material damage evolution and failure behavior under thermal-force coupling conditions. Infrared thermal radiation units in a confocal configuration were used to create ultra-high-temperature environments, offering advantages of compactness, rapid heating, and versatility. In situ tensile tests were conducted on C/SiC samples in a nitrogen atmosphere at both room temperature and 1200 °C. The high-resolution image data demonstrate various failure phenomena, such as matrix cracking and pore linkage. Image-based finite element simulations indicate that the temperature-dependent variation of the failure mechanism is attributable to thermal residual stresses and defect-induced stress concentrations. This work seamlessly integrates extreme mechanical testing methods with in situ observation techniques, providing a comprehensive solution for accurately quantifying crack initiation, pore connection, and failure behavior of C/SiC composites.

Failure and Strength of 2D-C/sic Composite under In-Plane Shear Loading at Elevated Temperatures

A Modified Iosipescu Method to Study In-Plane Shear Strength of C/SiC Composites at Elevated Temperatures in Air

Compressive Behavior of C/SiC Composites over a Wide Range of Strain Rates and Temperatures

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 1800 °C in Air

High-temperature tensile behavior of 3D SiC/SiC composites

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Tensile Properties of Two-Dimensional Carbon Fiber Reinforced Silicon Carbide Composites at Temperatures Up to 2300 °C

Experimental Study of High-Temperature Tensile Mechanical Properties of 3D Needled C/C–SiC Composites

High-temperature Flexural Mechanical Properties of SiC/SiC Composites

In Situ X-ray Imaging and Numerical Modeling of Damage Accumulation in C/SiC Composites at Temperatures Up to 1200 ℃

Transition of in-plane compressive strength and failure mechanism of 2D-C/SiC: Influence of off-axis loading angle and loading rate

Behavior of Two-Dimensional C/SiC Composites Subjected to Thermal Cycling in Controlled Environments

Modified Double-Notched Specimen for Ultra-High Temperatures Shear-Strength Testing of Carbon/carbon Composites

On the Tensile Behaviors of 2D Twill Woven SiO2f/SiO2 Composites at Ambient and Elevated Temperatures: Mesoscale Analysis and in Situ Experimental Investigation

Experimental and Numerical Study on the Bending Behavior of Satin-Woven SiCf/SiC Composites

Mechanical properties and microstructure evolution of 3D C f /SiBCN composites at elevated temperatures

Study of SiC fiber axial compressive behavior using tensile recoil measurement

An Experimental Study on the in Situ Strength of Sic Fibre in Unidirectional Sic/Al Composites

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

High-temperature constitutive model for three-dimensional needled C/C-SiC composite under tensile loading