Room-temperature compressive deformation behavior of Mg–Zn–Ca alloy processed by equal channel angular pressing
L.B. Tong,M.Y. Zheng,S.W. Xu,X.S. Hu,K. Wu,S. Kamado,G.J. Wang,X.Y. Lv
DOI: https://doi.org/10.1016/j.msea.2010.09.041
2010-01-01
Abstract:The ultra-fine grained (UFG) Mg–5.25 wt.% Zn–0.6 wt.% Ca alloy was processed by equal channel angular pressing (ECAP), and the coarse grained (CG) alloy was prepared by subsequent annealing treatment. The microstructure, texture evolution and mechanical properties of the UFG and CG alloys during compressive deformation at ambient temperature were investigated. The results indicated that the dislocation slip was dominant in the UFG Mg alloy, and the compressive yield stress (CYS) of the UFG alloy was higher than that of the CG alloy due to grain refinement. In the CG Mg alloy, the activation of tension twinning also occurred in addition to basal slip, the work hardening rate was increased because of twin-induced additional hardening. Dynamic recrystallization (DRX) was observed in the CG alloy compressed to large strains at ambient temperature. Most of the {0 0 0 2} planes in both UFG and CG Mg alloys were rotated gradually to be perpendicular to the compressive direction (CD). Keywords Ultra-fine grain (UFG) Coarse grain (CG) Equal channel angular pressing (ECAP) Mg–Zn–Ca alloy Compressive deformation 1 Introduction Magnesium and its alloys are potential candidate materials for structural components in automobile and aerospace industry because of their low density and high specific strength and stiffness [1] . However, Mg alloys exhibit poor ductility at room temperature, due to their limited slip systems available [2] . Grain refinement is an effective way to improve the mechanical properties of Mg alloys. During the recent decades, equal channel angular pressing (ECAP) has emerged as a widely known procedure for the fabrication of ultra-fine grained (UFG) metals and alloys by introducing very large strains during deformation processing [3] . Both the grain size and crystal orientation have significant influence on the deformation behavior of Mg alloys. At room temperature, in addition to dislocation slip, twinning deformation is an important deformation mechanism of Mg alloys since twinning system can accommodate c -axis strain. Two types of twins have often been reported in Mg alloys: {1 0 −1 2} plane tension and {1 0 −1 1} plane contraction twins [4] . Tension twins are formed during the tension parallel to c -axis or compression perpendicular to c -axis, while the contraction twins are active when the tensile direction is perpendicular to c -axis or compressive is parallel to c -axis [5] . The grain refinement in Mg alloys restricts the activation of twinning deformation [6] . Barnett et al. [7] observed a transition from twinning to slip dominated flow with decreasing grain size when an as-extruded Mg–3Al–1Zn alloy is subjected to compressive deformation. The fiber texture with (0 0 0 2) basal plane and 〈 1 0 −1 0〉 direction parallel to extrusion direction led to the activation of {1 0 −1 2} twinning when compressed along the extrusion direction, resulting in the lower compressive yield stress [8] . ECAP can refine the grain size and modify the texture of Mg alloys [9] , which will have a significant influence on the deformation behavior. del Valle et al. [10] investigated the influence of texture and grain size on work hardening rate during the tensile deformation of ECAPed AM60 alloy. They reported that grain refinement caused a strong decrease in work hardening rate, and the texture had a great influence on work hardening behavior, for example, the ideal orientation of the basal planes (inclined about 45° to tensile axis) in the ECAPed AM60 alloy hindered the activation of prismatic slip, leading to an additional strain hardening. Zheng et al. [11] investigated the compressive deformation of ECAPed Mg–Zn–Y–Zr alloy at 423 K, a short region with high strain hardening rate was followed by a long steady state region with very low strain hardening rate. They considered that both grain refinement and texture with basal plane inclined 45° to ECAP direction suppressed the twin deformation in the UFG Mg–Zn–Y–Zr alloy, which resulted in a distinct work hardening behavior. However, the systematic investigations on the compression deformation behavior of UFG Mg alloys processed by ECAP are still insufficient, especially the evolution of microstructure and texture during the deformation process. Alloying Mg with Ca increases the strength and corrosion resistance [12] , while the presence of Zn in the binary Mg–Ca alloys enhances the precipitation hardening response [13] , consequently, Mg–Zn–Ca alloy with fine stable precipitates in the matrix has attracted great attention as heat-resistant Mg alloy with low cost in the recent years [14] . In addition, Ca is a major component in human bone and can accelerate the bone growth [15] , thus Mg–Zn–Ca alloys have great potential for use in biodegradable and bioabsorbable implants [16] . In our previous work, the microstructural development and tensile properties of the UFG Mg–Zn–Ca alloy processed by ECAP have been studied [17,18] . The aim of this study is to investigate the deformation behavior of UFG and CG Mg–Zn–Ca alloys during the compression process at room temperature, with the main focus on the evolution of microstructure, texture and mechanical properties. 2 Experimental procedure The Mg–5.25 wt.% Zn–0.6 wt.% Ca alloy was extruded at 300 °C with a reduction ratio of 12. The as-extruded alloy was cut into billets with a dimension of 10 mm × 10 mm × 70 mm. The outer and interior angles of ECAP die were ψ = 37° and Φ = 90°, respectively. The ECAP processing was conducted at 250 °C for 8 passes (corresponding to a total strain of ɛ ≈ 8.4), using processing route Bc with constant displacement rate of 10 mm/s. Subsequently, the as-ECAPed alloy was annealed at 300 °C for 4 h to prepare the coarse grained (CG) alloy. The specimens for microstructural observation and texture analysis were cut along y -plane, which was parallel to extrusion and normal direction (ED and ND). The rod-shaped compressive specimens with a diameter of 7 mm and a length of 10.5 mm were machined from the UFG (as-ECAPed) and CG (as-annealed) alloys, with the longitudinal direction parallel to the ECAP direction (ED). The compression tests were carried out at room temperature with a strain rate of 1 mm/min up to different strains, the compressive direction (CD) was along the ED. After compressive tests, the planes parallel to compressive direction were selected for microstructure observation using a JEOL FESEM JSM-7000F Scanning Electron Microscopy (SEM) and a Philips-CM12 transmission electron microscope operating at 200 kV. The central region of specimen was selected for EBSD analysis, EBSD data were obtained from the same SEM equipped with TSL MSC-2200. 3 Results and discussions Fig. 1 shows the microstructure and texture of as-ECAPed and annealed Mg–Zn–Ca alloys. The as-ECAPed alloy exhibited a homogeneous UFG structure ( Fig. 1 a), the average grain size was calculated as 0.8 μm. Some elongated ellipsoidal grains were also observed, which was resulted from shear deformation during ECAP [18] . Most of {0 0 0 2} planes in the as-ECAPed alloy were inclined about 40° to ED, there also exists a weak fiber texture with {0 0 0 2} plane inclined about 10° to ED. After annealing treatment, equiaxed grain structure was observed, the average grain size was increased to about 6.0 μm ( Fig. 1 b). The main texture was changed only a little compared with the as-ECAPed alloy, most of {0 0 0 2} planes were inclined about 45° to ED, and the intensity of the fiber texture with {0 0 0 2} plane inclined about 10° to ED was slightly increased. The purpose of the annealing treatment is the attainment of samples with different grain size but retaining the similar texture. 3.1 Mechanical properties Fig. 2 shows the compressive stress vs. strain and work hardening rate curves of the UFG and CG alloys. For the UFG alloy, the compressive yield strength (CYS) was 200 MPa, where the CYS was defined as the 0.2% proof stress ( Fig. 2 a). The work hardening rate showed a first sharp decrease due to the elastoplastic transition ( Fig. 2 b). When the compressive strain was higher than 5%, the work hardening rate was decreased sharply due to the intensive dynamic recovery, which took place as a process of dislocation absorption in grain boundaries. This limited work hardening induced the premature plastic instabilities, which resulted in a poor elongation to failure (7%). Such phenomenon was also observed in our previous study on tensile behavior of UFG Mg–Zn–Ca alloy [17] . For the CG alloy, the CYS was decreased to 136 MPa, after the elastoplastic transition, work hardening rate was increased remarkably with increasing strain and retained a higher value than that in the UFG alloy, this intensive work hardening behavior in the CG alloy led to the ultimate compressive strength (UCS) of 412 MPa and the elongation to failure of 20%. This evolution of work hardening rate was related to the twinning deformation, which will be discussed in the following section. 3.2 Microstructure evolution Fig. 3 shows the microstructure of the UFG alloy with different compressive strains. The grain size of the specimens deformed to 3% ( Fig. 3 a) and 7% ( Fig. 3 b) strain was similar with that in the undeformed alloy (0.8 μm). No twins were observed in the specimens deformed to different strains. Fig. 4 shows the microstructure of the CG Mg–Zn–Ca alloy with different compressive strains. Compared with the initial microstructure ( Fig. 4 a), some lenticular type twins were observed in the specimen deformed to 3% strain ( Fig. 4 b), which were determined as tension twins by EBSD analysis (with a misorientation of 86.3° between the matrix and twinned lattice) [19] . Some twins traversed the whole original grains, resulting in the grain subdivision. As shown in Fig. 4 c and d, the fraction of twin area was decreased, and some finer grains were observed with increasing compressive strain. As shown in the TEM micrographs of the specimens compressed to failure, the dislocation density in the UFG alloy was much lower than that in the CG alloy ( Fig. 5 a and b), because the dislocations activated during compression were more easily absorbed by grain boundaries in UFG metals [20] . In addition to the zones with high dislocation density ( Fig. 5 b), the zones with fine equiaxed grains ( Fig. 5 c) were also observed in the CG alloy compressed to failure. This suggested that dynamic recrystallization (DRX) occurred in local regions after compressed to high strains at room temperature. Such dynamic recrystallization behavior has been reported in AZ31 Mg alloy after compressed up to 11% at room temperature [2] and high purity magnesium after cold rolling when the reduction rate was larger than about 30% [21] . The stress concentration at local area due to the pile-up of dislocations during deformation might result in the cross-slip and annihilation of dislocation, which caused the recrystallization [21] . In the current study, lots of dislocations were accumulated in the original grains and formed some dislocation cells ( Fig. 5 b). With increasing compressive strain, the misorientation between the cells was increased and resulted in continuous dynamic recrystallization in some area with high stress concentration. Fig. 6 shows the evolution of misorientation angle in the CG alloy during the compression. The fraction of 86° misorientation angle was increased from 14.0% ( Fig. 6 a) to 26.8% ( Fig. 6 b) in the specimen deformed to 3% strain, which was resulted from the activation of tension twins. In the specimens deformed to 11% strain and to failure, the fraction of low angle grain boundaries (LAGBs) was increased, which might be resulted from the dynamic recovery induced by the dislocation accumulation. 3.3 Effect of twinning activation on the mechanical properties The twinning activation was not observed in the UFG alloy during compressive test at room temperature. The energy of twin interfaces was significantly large in Mg alloy, which led to the increasing difficulty in twin nucleation with decreasing grain size [22] . Moreover, the critical resolved shear stress (CRSS) of twinning deformation was increased with the decrease of grain size [2] . Therefore, grain refinement restricted the twin activation in the Mg–Zn–Ca alloy. In the UFG alloy, the orientation of most grains was favorable for basal slip, and the average Schmid factor for basal slip ({0 0 0 1} 〈1 1 −2 0〉) was calculated as 0.303. Using this factor and CYS of 200 MPa, a CRSS of about 60 MPa was estimated, which was consistent with the CRSS for basal slip in Mg alloys [23] . This indicated that the initial stage of compressive deformation at room temperature was mainly carried out by the basal slip in the UFG alloy. In contrast, for the CG alloy, some tension twins were observed in the specimen deformed to 3% strain, indicated that twinning occurred during the compressive deformation. The orientation of most grains was more favorable for basal slip, while the weak texture with {0 0 0 2} plane inclined about 10° to ED was favorable for the activation of tension twin. Thus, in current study, twins were observed only in a few grains with a favorable orientation for tensile twinning, and their fraction was much lower than that of the extruded Mg alloys compressed along ED [2] , in which most of the grains had a preferential orientation for tension twinning. Moreover, the average Schmid factor for the activation of tension and contraction twin in the CG alloy was calculated as 0.3562 and 0.4026 by EBSD analysis. Because the CRSS for the contraction twin is relatively large [24] , the activation of contraction twin was difficult even with high Schmid factor, and contraction twinning was not observed. As a result, both the dislocation slip and tension twinning were activated in the CG alloy during compressive test. The low work hardening rate at low compressive strain (less than 3%) of the CG alloy may be resulted from the activation of tensile twinning. Such phenomenon has been observed in the rolled AZ31 Mg alloy when compressed along the rolling direction [25] . Moreover, it has been reported that twin also induces three additional hardening effect at large strains: twin introduces additional barriers to dislocation movement, reorients the lattice to “hard” crystallographic orientation and leads to the establishment of high hardening rates in the twin interior when the transformation of dislocations pass through twinning front [7] . Therefore, the obviously increased work hardening rate of the CG alloy above 3% strain may be induced by the additional hardening effect of twins. 3.4 Texture evolution Fig. 7 shows the texture evolution of the UFG Mg–Zn–Ca alloy during the compression. For initial texture, most of {0 0 0 2} planes were inclined about 40° to ED. After compressed to 3% strain, the orientation of {0 0 0 2} plane changed only a little, inclined about 41° to ED. In the fractured specimen, {0 0 0 2} planes were inclined 48° to ED. It was concluded that the {0 0 0 2} plane was rotated gradually to be perpendicular to the compressive direction (CD) during the compression. Fig. 8 shows the texture evolution of the CG Mg–Zn–Ca alloy. During the compressive test, most of {0 0 0 2} planes were also rotated gradually to be perpendicular to the compressive direction. Most of the {0 0 0 2} plane in the fractured specimen ( Fig. 8 d) was located nearly perpendicularly to CD because of the high compressive strain to failure (20%). As shown by ellipse in Figs. 7b and 8b , it should be noted that after compressed to 3% strain, the intensity of texture component with {0 0 0 2} plane perpendicular to CD in CG alloy was much higher than that in UFG alloy. This may be ascribed to the higher intensity of the texture with {0 0 0 2} plane inclined about 10° to ED and larger grain size, both of which are favorable to tensile twinning, leading to a rapid texture change in the CG alloy. The texture evolution in both UFG and CG alloy was gradual with strain, which suggested that dislocation slip was the main deformation mechanism of the CG and UFG alloy during compression at ambient temperature. The relationship between the texture evolution and dislocation slip of the Mg–Zn–Ca alloys under compression test needs to be further investigated. 4 Conclusions (1) In the UFG Mg–Zn–Ca alloy, dislocation slip plays an important role in the compressive test at room temperature, and twinning deformation is not observed. The work hardening rate is very low after elastoplastic transition, resulting in the poor ductility. (2) In the CG alloy, both twinning activation and dislocation slip occur during compression. The higher work hardening rate after elastoplastic transition improves the ductility. DRX occurs in the specimen compressed to large strains. (3) In both UFG and CG alloy, most of {0 0 0 2} planes are rotated gradually to be perpendicular to the compressive direction during compressive deformation. The texture change is more remarkable at low strains in the CG alloy due to the twinning deformation. Acknowledgements This work is supported by the National Natural Science Foundation of China (No. 50201005 and No. 50571031 ), the Program for New Century Excellent Talents in University (NCET-08-0169), International S&T Cooperation Key Project of Ministry of Science and Technology of China ( 2010DFB50210 ) and International S&T Cooperation Key Project of Heilongjiang Province, China (WB09A202). References [1] S.E. Ion F.J. Humphreys S.H. White Acta Metall. 30 1982 1909 1919 [2] Y. Chino K. Kimura M. Mabuchi Mater. Sci. Eng. A 486 2008 481 488 [3] R.Z. Valiev T.G. Langdon Prog. Mater. Sci. 51 2006 881 981 [4] Q. Yang A.K. Ghosh Acta Mater. 54 2006 5159 5170 [5] L. Jiang J.J. Jonas R.K. Mishra A.A. Luo A.K. Sachdev S. Godet Acta Mater. 55 2007 3899 3910 [6] J.T. Wang D.L. Yin J.Q. Liu J. Tao Y.L. Su X. Zhao Scr. Mater. 59 2008 63 66 [7] M.R. Barnett Z. Keshavarz A.G. Beer D. Atwell Acta Mater. 52 2004 5093 5103 [8] S. Kleiner P.J. Uggowitzer Mater. Sci. Eng. A 379 2004 258 263 [9] W.J. Kim S.I. Hong Y.S. Kim S.H. Min H.T. Jeong J.D. Lee Acta Mater. 51 2003 3293 3307 [10] J.A. del Valle F. Carreño O.A. Ruano Acta Mater. 54 2006 4247 4259 [11] M.Y. Zheng S.W. Xu X.G. Qiao K. Wu S. Kamado Y. Kojima Mater. Sci. Eng. A 483–484 2008 564 567 [12] E. Zhang L. Yang Mater. Sci. Eng. A 497 2008 111 118 [13] J.F. Nie B.C. Muddle Scr. Mater. 37 1997 1475 1481 [14] G. Levi S. Avraham A. Zilberov M. Bamberger Acta Mater. 54 2006 523 530 [15] C.M. Serre M. Papillard P. Chavassieux J.C. Voegel G. Boivin J. Biomed. Mater. Res. 42 1998 626 633 [16] M.P. Staiger A.M. Pietak J. Huadmai G. Dias Biomaterials 27 2006 1728 1734 [17] L.B. Tong M.Y. Zheng H. Chang X.S. Hu K. Wu S.W. Xu S. Kamado Y. Kojima Mater. Sci. Eng. A 523 2009 289 294 [18] L.B. Tong M.Y. Zheng X.S. Hu K. Wu S.W. Xu S. Kamado Y. Kojima Mater. Sci. Eng. A 527 2010 4250 4256 [19] J. Koike Metall. Mater. Trans. A 36 2005 1689 1696 [20] Y.G. Ko D.H. Shin K.-T. Park C.S. Lee Scr. Mater. 54 2006 1785 1789 [21] M. Jotoku A. Yamamoto H. Tsubakino J. Jpn. Inst. Light Met. 56 2006 711 715 [22] J. Koike T. Kobayashi T. Mukai H. Watanabe M. Suzuki K. Maruyama K. Higashi Acta Mater. 51 2003 2055 2065 [23] D.K. Xu L. Liu Y.B. Xu E.H. Han Scr. Mater. 58 2008 1098 1101 [24] B.C. Wonsiewicz W.A. Backofen Trans. Metall. Soc. AIME 239 1967 1422 1431 [25] Y.N. Wang J.C. Huang Acta Mater. 55 2007 897 905