Abstract:In this study, equal channel angular pressing (ECAP) was applied to a hot-extruded Mg–5.00Zn–0.92Y–0.16Zr (wt.%) alloy to produce an ultrafine-grained a-Mg structure of 0.6μm with uniformly distributed fine quasicrystal Mg3YZn6 particles. The basal planes in the as-ECAPed alloy were inclined approximately 45° to the ECAP direction (EPD); thus, a high Schmid factor of 0.36 for (0001)〈112¯0〉 basal slip along EPD was obtained. Then, the superplastic behavior at low temperatures of 150–250°C and initial strain rates of 1.67×10−3s−1–1.67×10−1s−1 of the as-ECAPed alloy was investigated and compared with that of the as-extruded alloy. The microstructural development, texture evolution and cracking behavior during tensile tests were systemically investigated by electron backscattered diffraction (EBSD) analysis. During the tensile test along the EPD, the basal planes in the as-ECAPed alloy specimen were tilted approximately 15° away from the original position; thus, the basal planes were still in a position favorable for the basal slip along the EPD. As a result, a maximum elongation of 865% was obtained at 200°C and a strain rate of 1.67×10−3s−1, as a result of this favored basal texture and the excellent thermal stability of the ultrafine-grained structure. This optimum superplastic temperature of 200°C is much lower than that obtained for other Mg–Zn–Y–(Zr) alloys. In contrast, for the as-extruded alloy specimen, superplastic behavior did not occur until the critical condition of 250°C and a strain rate of 1.67×10−3s−1. Below this temperature and strain rate, the strong extrusion basal texture was maintained, and the cracks in the hot-worked coarse region (or un-DRXed region) were observed nucleating mainly associated with the formation of a 38° {101¯1}–{101¯2} double twin. At this temperature and strain rate, the hot-worked coarse regions were significantly refined by the dynamic recovery and the following recrystallization process. In the case, the formation of a double twin was prevented and the facture was delayed.

Compressive Behavior of Ultrafine-Grained Mg-Zn-Y-Zr Alloy Containing Quasicrystalline Phase

Compressive Deformation of Mg–Zn–Y–Zr Alloy Processed by Equal Channel Angular Pressing

Superplasticity of Mg–Zn–Y Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Hot Compression Deformation Behavior of Mg-Zn-Al-(Y) Alloys Reinforced with Quasicrystal

Microstructure and Tensile Properties of A Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

The Microstructural Evolution and Superplastic Behavior at Low Temperatures of Mg–5.00Zn–0.92Y–0.16Zr (wt.%) Alloys after Hot Extrusion and ECAP Process

Equal Channel Angular Pressing Of Magnesium Alloy Containing Quasicrystal Phase

Microstructure and Mechanical Properties of Squeeze Casting Quasicrystal Reinforced AZ91D Magnesium Matrix Composites

Compressive deformation behavior of ultrafine-grained Mg-3Zn-1.2Ca-0.6Zr alloy at room temperature

Microstructure and Mechanical Properties of Ultrafine Grained Mg97Y2Zn1 Alloy Processed by Equal Channel Angular Pressing

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

High Temperature Compressive Deformation Behavior of an Extruded Mg–8Gd–3Y–0.5Zr (wt.%) Alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Microstructure and Mechanical Properties of Mg–Zn–Ca Alloy Processed by Equal Channel Angular Pressing

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Hot Deformation Behavior of Mg-Zn-Gd-Y Base Alloys with Different Contents of Quasicrystal

Superplasticity of Mg-5.8Zn-1Y-Zr Alloy Sheet Fabricated by Combination of Extrusion and Hot-Rolling Processes

Effect of Hot Extrusion on Microstructure and Mechanical Properties of Quasicrystal-Reinforced Mg-Zn-Y Alloy

Deformation Behavior, Microstructure Evolution and Hot Workability of Mg-3.7Gd-2.9Y-0.7Zn-0.7Zr Alloy

Strengthening and Toughening Mechanisms of an Ultrafine Grained Mg-Gd-Y-Zr Alloy Processed by Cyclic Extrusion and Compression

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure