Abstract:In this study, equal channel angular pressing (ECAP) was applied to a hot-extruded Mg–5.00Zn–0.92Y–0.16Zr (wt.%) alloy to produce an ultrafine-grained a-Mg structure of 0.6μm with uniformly distributed fine quasicrystal Mg3YZn6 particles. The basal planes in the as-ECAPed alloy were inclined approximately 45° to the ECAP direction (EPD); thus, a high Schmid factor of 0.36 for (0001)〈112¯0〉 basal slip along EPD was obtained. Then, the superplastic behavior at low temperatures of 150–250°C and initial strain rates of 1.67×10−3s−1–1.67×10−1s−1 of the as-ECAPed alloy was investigated and compared with that of the as-extruded alloy. The microstructural development, texture evolution and cracking behavior during tensile tests were systemically investigated by electron backscattered diffraction (EBSD) analysis. During the tensile test along the EPD, the basal planes in the as-ECAPed alloy specimen were tilted approximately 15° away from the original position; thus, the basal planes were still in a position favorable for the basal slip along the EPD. As a result, a maximum elongation of 865% was obtained at 200°C and a strain rate of 1.67×10−3s−1, as a result of this favored basal texture and the excellent thermal stability of the ultrafine-grained structure. This optimum superplastic temperature of 200°C is much lower than that obtained for other Mg–Zn–Y–(Zr) alloys. In contrast, for the as-extruded alloy specimen, superplastic behavior did not occur until the critical condition of 250°C and a strain rate of 1.67×10−3s−1. Below this temperature and strain rate, the strong extrusion basal texture was maintained, and the cracks in the hot-worked coarse region (or un-DRXed region) were observed nucleating mainly associated with the formation of a 38° {101¯1}–{101¯2} double twin. At this temperature and strain rate, the hot-worked coarse regions were significantly refined by the dynamic recovery and the following recrystallization process. In the case, the formation of a double twin was prevented and the facture was delayed.

Characterization of microstructure in high strength Mg 96Y 3Zn 1 alloy processed by extrusion and equal channel angular pressing

Microstructure and Mechanical Properties of Mg96Y3Zn1 Alloy Processed by Equal Channel Angular Pressing

Microstructure and Mechanical Properties of Ultrafine Grained Mg97Y2Zn1 Alloy Processed by Equal Channel Angular Pressing

Microstructural Evolution and Mechanical Properties of Mg95.5Y3Zn1.5 Alloy Processed by Extrusion and ECAP

High Strength Mg_(97)Y_2Zn_1 Alloy Processed by Extrusion and Equal Channel Angular Pressing

Microstructure and Tensile Properties of A Mg-Zn-Y-Zr Alloy Containing Quasicrystal Phase Processed by Equal Channel Angular Pressing

Microstructure Evolution and Mechanical Properties of Mg-Gd-Y-Zn-Zr Alloy During Equal Channel Angular Pressing

Microstructure Evolution and Mechanical Behavior of Mg-10Gd-3Y-0.4Zr Alloy Processed by ECAP at High Temperature

Preparation, Microstructure Evolutions, And Mechanical Property Of An Ultra-Fine Grained Mg-10gd-4y-1.5zn-0.5zr Alloy

Microstructure and Mechanical Properties of Za62 Mg Alloy by Equal-Channel Angular Pressing

Ductility enhancement in Mg–8.7Gd–4.18Y–0.42Zr magnesium alloy fabricated through extrusion and equal channel angular pressing (EX-ECAP)

The Microstructural Evolution and Superplastic Behavior at Low Temperatures of Mg–5.00Zn–0.92Y–0.16Zr (wt.%) Alloys after Hot Extrusion and ECAP Process

Development of a High-Strength Mg Alloy with Superior Ductility Through a Unique Texture Modification from Equal Channel Angular Pressing

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Microstructure and Mechanical Properties of Mg–Zn–Ca Alloy Processed by Equal Channel Angular Pressing

Microstructure and mechanical properties of Mg-Gd-Y-Zr alloy processed by equal channel angular pressing

Precipitation behaviors and mechanical properties of a solution-treated Mg-Gd-Nd-Zn-Zr alloy during equal-channel angular pressing process

Effect of Multi-Pass Equal Channel Angular Pressing on the Microstructure and Mechanical Properties of a Heterogeneous Mg88Y8Zn4 Alloy

The Effect of Particles on Microstructure and Mechanical Behaviour of Mg-10Gd-3Y-0.4Zr Alloy Processed by ECAP

Ultra-fine Grained Mg-Zn-Ca-Mn Alloy with Simultaneously Improved Strength and Ductility Processed by Equal Channel Angular Pressing

Microstructure Evolution and Mechanical Properties of Mg-LPSO Two Phase Mg96Y2Ni2 (at. %) Alloy Processed by Hot Extrusion and Decreasing-Temperature ECAP