Abstract:With types of in-house-synthesized multi-walled carbon nanotubes (CNTs) and the nitrates of the corresponding metallic components, highly active CNT-promoted Cu–ZnO–Al2O3 catalysts, symbolized as CuiZnjAlk-x%CNTs, were prepared by the co-precipitation method. Their catalytic performance for methanol synthesis from H2/CO/CO2 was studied and compared with the corresponding CNT-free co-precipitated catalyst, CuiZnjAlk. It was shown experimentally that appropriate incorporation of a minor amount of the CNTs into the CuiZnjAlk could significantly increase the catalyst activity for methanol synthesis. Under the reaction conditions of 493 K, 5.0 MPa, H2/CO/CO2/N2 = 62/30/5/3 (v/v), GHSV = 8000 h-1, the observed CO conversion and methanol formation rate over a co-precipitated catalyst of Cu6Zn3Al1-12.5%CNTs reached 36.8% and 0.291 μmol CH3OH s-1 (m2-surf. Cu)-1, which was about 44 and 25% higher than those (25.5% and 0.233 μmol CH3OH s-1 (m2-surf. Cu)-1) over the corresponding CNT-free co-precipitated catalyst, Cu6Zn3Al1. Addition of a minor amount (10–15 wt%) of the CNTs to the Cu6Zn3Al1 catalyst was found to considerably increase specific surface area, especially Cu surface area of the catalyst. H2-TPD measurements revealed that the CNTs and the pre-reduced CNT-promoted catalyst systems could reversibly adsorb and store a considerably greater amount of hydrogen under atmospheric pressure at temperatures ranging from room temperature to ∼573 K. This unique feature would be beneficial for generating microenvironments with higher stationary-state concentration of active hydrogen adspecies on the surface of the functioning catalyst, especially at the interphasial active sites since the highly conductive CNTs might promote hydrogen spillover from the Cu sites to the Cu/Zn interphasial active sites, and thus be favorable for increasing the rate of the CO hydrogenation reactions. Alternatively, the operation temperature for methanol synthesis over the CNT-promoted catalysts can be 15–20 degrees lower than that over the corresponding CNT-free contrast system. This would contribute considerably to an increase in equilibrium CO conversion and CH3OH yield. The results of the present work indicated that the CNTs could serve as an excellent promoter.

A Highly Efficient Hybrid Catalyst for ″One-Pot″ Two-step Catalytic Synthesis of Dimethyl Ether from (CO2+H2) Via CH3OH

Preparation, Structure And Performance Of [Cuo-Zno-Al2o3]/[Hzsm-5] Core-Shell Bifunctional Catalysts For One-Step Synthesis Of Dimethyl Ether From Co2+H-2

Dimethyl Ether Synthesis from CO2 Hydrogenation on a CuO−ZnO−Al2O3−ZrO2/HZSM-5 Bifunctional Catalyst

Catalysis for One-step Synthesis of Dimethyl Ether from Hydrogenation of CO

Mechanism and catalytic performance for direct dimethyl ether synthesis by CO2 hydrogenation over CuZnZr/ferrierite hybrid catalyst

Core-shell structured CuO-ZnO@H-ZSM-5 catalysts for CO hydrogenation to dimethyl ether

A novel bifunctional catalyst obtained by in situ introduction of hierarchically structured HZSM-5 for direct DME synthesis from CO 2 hydrogenation

One-step synthesis of dimethyl ether from biomass-derived syngas on CuO-ZnO-Al2O3/HZSM-5 hybrid catalyst: Combination method, synergistic effect, water-gas shift reaction and catalytic performance

Optimizing CO 2 Hydrogenation to DME through Tailored Interfacial Interactions: Weakening Synergy in CuZnZr and Al-Modified SBA-15 Catalysts

Dimethyl Ether Synthesis from Co2 Hydrogenation over Cuo-Tio2-Zro2/Hzsm-5 Catalysts

Direct Synthesis of Dimethyl Ether on Supported Cu-Mn Catalysts

Long Carbon Nanotubes Intercrossed Cu/Zn/Al/Zr Catalyst for CO/CO2 Hydrogenation to Methanol/dimethyl Ether

Effect of the Hydrogenation Components on Copper-Based Catalysts for Synthesis of Dimethyl Ether from CO2 Hydrogenation

Insights Into the one‐Step Dimethyl Ether Carbonylation to Ethanol Over Cu/ZnO@Cu‐MOR Core‐Shell Catalysts with Porogen Engagement

Highly Active CNT-Promoted Cu–ZnO–Al2O3 Catalyst for Methanol Synthesis from H2/CO/CO2

Single-Step Synthesis of Dimethyl Ether from Biomass-Derived Syngas over Cuo-Zno-Mox (M = Zr, Al, Cr, Ti)/Hzsm-5 Hybrid Catalyst: Effects of Mox

Study on Catalyst C207-HZSM-5 for Dimethyl Ether Synthesis

Characterization of Cu-Mn/Zeolite-Y Catalyst for One-Step Synthesis of Dimethyl Ether from Co-H-2

A highly efficient Cu/ZnOx/ZrO2 catalyst for selective CO2 hydrogenation to methanol

Synthesis of Dimethyl Ether (DME) on Modified HY Zeolite and Modified HY Zeolite-Supported Cu–Mn–Zn Catalysts

Catalytic activity for direct CO2 hydrogenation to dimethyl ether with different proximity of bifunctional Cu-ZnO-Al2O3 and ferrierite