Manganese Oxide-based Mesoporous Thin-Film Electrodes: Manganese Disproportionation Reaction in Alkaline Media
Irmak Karakaya Durukan,Işıl Ulu,Ömer Dag,Irmak Karakaya
DOI: https://doi.org/10.1039/d3ta07973b
IF: 11.9
2024-02-02
Journal of Materials Chemistry A
Abstract:Abundant availability, reduced toxicity, and good thermal stability distinguish and make the manganese-based materials special in clean energy production and storage applications, when compared to the other transition metal-based materials. However, the manganese-base electrodes are not stable and undergo both Mn(III) and Mn(VI) disproportionation reactions under alkaline and/or acidic media. In this study, we explore the disproportionation reaction mechanism in alkaline media during oxygen evolution reaction (OER) utilizing mesoporous electrodes, namely LiMn2O4 (m-LMO), Mn3O4 (m-Mn3O4), and Mn2P2O7 (m-MnPP). These electrodes are crafted through the molten salt-assisted self-assembly (MASA) process. The procedure commences with the application of a metal salt(s)-surfactant and metal salt-pyrophosphoric acid-surfactant (where the surfactant is P123) lyotropic liquid crystalline mesophase coating over FTO surface by employing a clear ethanol or aqueous solution of the ingredients, followed by a subsequent calcination step at 300 oC. The m-LMO and m-Mn3O4 electrodes are characterized by spectroscopic, diffraction, imaging, and electrochemical techniques. At low electrochemical potentials, the Mn(III), and at more positive potentials, the Mn(VI) disproportionation reactions make these materials highly unstable in an alkaline media. The aforementioned degradations have been investigated by examination of the electrodes both prior to and subsequent use in electrochemical measurements (such as multiple cyclic voltammetry (m-CV) and multiple chronopotentiometry (m-CP)), conducted in various electrolytes. We found that the degradation process is relatively slow in the m-LMO, but elevated in the m-Mn3O4 and m-MnPP electrodes. The m-LMO is fully converted into the λ-MnO2 phase upon its oxidation and more robust to decomposition; making it ultra-thin further improves its robustness. However, the m-Mn3O4 and m-MnPP electrodes behave similar to each other and degrade more quickly (more pronounced in the later), by releasing purple-colored permanganate ions to the electrolyte media. A Mn(VI) disproportionation reaction mechanism is suggested using the experimentally gathered spectroscopic, diffraction, and electrochemical data. Formation of the Mn(VI) surface species and their electronegativity play vital roles in the disproportionation reaction.
materials science, multidisciplinary,chemistry, physical,energy & fuels