Abstract:Electropolishing has found wide application as the final surface treatment of metal products in mechanical engineering and instrumentation, medicine and reflective concentrators for PV cells. It was found that electropolishing (EP) not only reduces the surface roughness and changes its appearance, but improves many operational characteristics as well, such as corrosion resistance, endurance, tensile strength, and many others, and also changes the physicochemical properties, for example, reflectivity, electromagnetic permeability and electronic emission of some ferro-magnetic metals. This fact greatly expands the possibility of using this method in various fields of science and technology. This work is part of a study, examining electro polishing for reducing the crystalline defects adjacent to the surface, thus improving its physical properties, contributing to higher optical efficiency, when used in PV generation and storage devices. Five compositions were examined using different temperature and current density parameters. The polished samples were evaluated using reflectance spectrometry. The solution which was composed of Phosphoric acid - 85%, Acetic acid - 10%, Nitric acid - 5% was found to provide the best results. Another result obtained was that reflectance increased as the current density increased up to 25 A/dm2. Further increasing the current density resulted in deterioration of the surface and reduced reflectance. It was shown that careful lapping and polishing followed by electropolishing using the suggested solution may consist of an adequate treatment for preparing reflective concentrators for PV cells.

Patterning Polycrystalline Aluminum by Electropolishing at Low Voltages

Large-area self-ordered aluminium sub-micrometre dot arrays prepared by electropolishing on polycrystalline aluminium at constant current

A Facile Approach to Preparation of Nanostripes on the Electropolished Aluminum Surface

Afm Study of Quasi-Ordered Stripe-Like Nanostructures on Surfaces of Aluminum

Crystallographic Orientation Dependence of Nanopattern Morphology and Size in Electropolished Polycrystalline and Monocrystalline Aluminum: An EBSD and SEM Study

Voltage Dependence of Nanopattern Morphology in Electropolished Aluminum: A Theoretical Study

Voltage Dependence of Nanopattern Morphology and Size in Electropolished Monocrystalline Aluminum: An Experimental Study

Characterizing and optimizing the electropolishing and pore arrangement in porous anodic aluminum oxide (AAO)

Preparation and Annealing-Induced Structural Transition of Self-Organized Nanostripes on the Electropolished Aluminium Surface

Formation of Self-Assembled Stripes on the Anodic Aluminum Oxide

Self-assembled stripes on the anodic aluminum oxide by atomic force microscope observation

Effect of Al Polishing Conditions on the Growth and Morphology of Porous Anodic Alumina Films

Fabrication of Anodic Aluminum Oxide Templates with Small Interpore Distances

Highly Ordered Nanoscale Patterns on Anodic Aluminum Oxide (AAO) Surface

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts

Electropolishing of single crystal and polycrystalline aluminum to achieve high optical and mechanical surfaces

Electrochemical Polishing of 7075 Al Alloy in Phosphoric Acid

Influence of Acid Pickling on Electrodeposition of Aluminum on Magnesium Alloy in Room Temperature Molten Salts

Preparation and Study of Ordered Porous Anodic Alumina Film

Porous Alumina Films with Width-Controllable Alumina Stripes

Graining Technology by Electrolytic Etching on the Surface of Aluminum Alloys