Abstract:Aluminum foils with two different surface topographic textures were anodically oxidized at constant current in a phosphoric acid bath. In situ atomic force microscopy (AFM) was used to follow the initial development of surface topography on a 1 μm scale, during the early stages of porous oxide film formation. Microscopic convex features such as ridges on both foils begin to increase in height and width when the anodic film thickness exceeds the initial feature height. Equations of a mathematical model are presented incorporating established interfacial reactions and oxide conduction behavior. The model indicates that the film‐solution interface recedes into the metal during anodizing, since the current efficiency for oxide formation is smaller than the oxygen ion transport number in the film. Ridge surfaces increase in height due to the higher local conduction resistance to the film‐solution interface, while film deposits rapidly at ridges because of the low local resistance to the metal‐film interface. In agreement with the AFM results, enhanced oxide growth at ridges should start when the potential field in the film becomes two‐dimensional, as a result of the film growing to a thickness larger than the ridge height. © 2000 The Electrochemical Society. All rights reserved.

Self-assembled stripes on the anodic aluminum oxide by atomic force microscope observation

Formation of Self-Assembled Stripes on the Anodic Aluminum Oxide

Afm Study of Quasi-Ordered Stripe-Like Nanostructures on Surfaces of Aluminum

Preparation and Annealing-Induced Structural Transition of Self-Organized Nanostripes on the Electropolished Aluminium Surface

Highly Ordered Nanoscale Patterns on Anodic Aluminum Oxide (AAO) Surface

Anodizing Behavior Of Aluminum Foil Patterned With Sio2 Mask

Atomic Force Microscopy Study of the Initial Stages of Anodic Oxidation of Aluminum in Phosphoric Acid Solution

Novel self-assembled nanostructured alumina array with nanoscale grooves

A Facile Approach to Preparation of Nanostripes on the Electropolished Aluminum Surface

Self-assembly of Diverse Alumina Architectures and Their Morphology-Dependent Wettability

Investigation of the Pore Formation in Anodic Aluminium Oxide

Self-organized Formation of Hexagonal Nanopore Arrays in Anodic Alumina

Fabrication and Application of Alumina Nanoscale Ordered Array Template

Controllable Fabrication and Microstructure Modulation of Unique Aao Structures Based on Patterned Aluminum Surface

Unstable growth of anodic aluminum oxide investigated by AFM

Formation Mechanism of Porous Anodic Aluminium and Titanium Oxides

Mechanisms For Formation Of A One-Dimensional Horizontal Anodic Aluminum Oxide Nanopore Array On A Si Substrate (Vol 152, D227, 2005)

Preparation and Study of Ordered Porous Anodic Alumina Film

Controlled self-cleaning aluminum surfaces mediated by anodic aluminum oxide

Formation of Anodic Aluminum Oxide with Serrated Nanochannels.

Patterning Polycrystalline Aluminum by Electropolishing at Low Voltages