Abstract:Suspension effect poses a big threat to the integrity and safety of corroded pipelines. In this work, a finite element (FE) based multi-physics field coupling model was developed to determine the mechano-electrochemical (M-E) interaction at an external corrosion defect on a suspended X100 steel pipe and predict its failure pressure. Theoretical calculations were used for model validation. Parameter effects including the defect location on the pipe, geometry of the defect, suspension length and pipe burial depth were determined. Results demonstared that, generally, the M-E effect at corrosion defect caused an increased stress concentration and anodic current density (i.e., corrosion rate), decreasing the failure pressure of the pipeline. The effect became more apparent when the pipe was in suspension. Both the stress and the anodic current density at the corrosion defect were dependent on the defect geometry, especially the defect depth. When the depth was up to 40% of pipe wall thickness, the von Mises stress exceeded the yield stress of the steel, causing local plastic deformation. A critical defect length of <math>20Dt</math> (D is the outer diameter of the pipe and t is pipe wall thickness) existed, below which the von Mises stress and the anodic current density at the corrosion defect increased with increased defect length. When the defect length exceeded the critical value, the effect was not obvious. An increased suspension length of the pipe would elevate the local stress and anodic current density at the corrosion defect, reducing the failure pressure of the pipe. A critical pipe burial depth of 2.5 m was identified, exceeding which the failure pressure of the pipe decreased rapidly with the increased burial depth. When the burial depth was smaller than 2.5 m, the effect was marginal. The location of the corrosion defect on the pipe did not affect the local stress, anodic current density and failure pressure at an appreciable level, and could be ignored in defect assessment on suspended pipelines.

Calculation of Diffusivity of Point Defects in Passive film Formed on X80 Pipeline Steel

Influences of temperature, pH value and chloride ion on the diffusivity of point defect in the passive film on X80 pipeline steel

Diffusivity of Point Defects in the Passive Film on a Ni16Cr13Co4Mo Alloy in Molten NaCl-Na2SO4

INFLUENCE OF TEMPERATURE ON THE ELECTROCHEMICAL PROPERTY OF PASSIVE FILM FORMED ON X80 PIPELINE STEEL

Calculation and comparison between alternate and continuous controlled cooling technology for X65 pipeline steel plate

Diffusivity of the point defects in the passive film on a Ni16Cr13Co4Mo alloy in molten NaCl-Na 2 SO 4

Diffusivity of a Point Defect in the Passive Film on Ti with Plastic Deformation in 3.5% NaCl Solution

Electronic Properties of the Passive Films Growth on Cu-Ni Alloy from the Viewpoint of Point Defect Model and Power-Law Model

Estimation of Some Parameters in the Point Defect Model (PDM) for the Passivity of Metals.

Finite element modeling of corrosion defect growth and failure pressure prediction of pipelines

Influence of Potentiostatic Aging, Temperature and Ph on the Diffusivity of a Point Defect in the Passive Film on Nb in an HCl Solution

Failure pressure prediction by defect assessment and finite element modelling on natural gas pipelines under cyclic loading

Research on Failure Pressure of API 5L X100 Pipeline with Single Defect

Investigation by numerical modeling of the mechano-electrochemical interaction of circumferentially aligned corrosion defects on pipelines

Corrosion behavior of X80 pipeline steel local defect pits under static liquid film

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Analytical prediction of failure pressure for pipeline with long corrosion defect

Failure analysis of natural gas buried X65 steel pipeline under deflection load using finite element method

Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction

Simulation of the Hydrogen Permeation Behavior of X80 Pipeline Steels in H<sub>2</sub>S Saturated Environment by Cathodic-Charging Method

Failure assessment of X80 pipeline with interacting corrosion defects