Diffusivity of the point defects in the passive film on a Ni16Cr13Co4Mo alloy in molten NaCl-Na 2 SO 4

Jiahao Wang,Dangguo Li,Tianmin Shao

DOI: https://doi.org/10.1016/j.corsci.2023.111456

IF: 7.72

2023-08-13

Corrosion Science

Abstract:Passive films were prepared at different film formation potential (E ff ) on a Ni16Cr13Co4Mo alloy in NaCl-Na 2 SO 4 eutectic at 700 °C. The electrochemical property of the passive film was measured and the diffusivity (D 0 ) of the point defects in the passive film was calculated based on point defect model (PDM), which was around 10 −14 cm 2 /s. TEM and XPS proved that passive film was composed of outer Na 2 CrO 4 -Cr 2 O 3 mixture, middle Cr 2 O 3 -TiO 2 mixture, and inner amorphous Al 2 O 3 . With increased E ff , the passive film became compact and had better crystallinity. The corrosion mechanism of the alloy under potentiostatic condition was discussed.

materials science, multidisciplinary,metallurgy & metallurgical engineering