Abstract:Silicon carbon nitride (SiCN) films were deposited by dual ion beam sputtering (DIBS) of SiC target in mixed Ar/N2 atmosphere at 100°C. The surface roughness and the mechanical properties of the SiCN films were measured by using non-contact surface profilometer and nano-indenter. The bonding structure for the SiCN films was analyzed using Fourier transform infrared spectroscopy (FTIR), Raman spectroscopy and X-ray photoelectron spectroscopy (XPS), respectively. The influences of assisting ion beam energy and concentration on surface roughness, mechanical properties and bonding structure of the SiCN films were discussed systematically. The results showed that the variations of surface roughness and hardness for the SiCN films with the assisting ion beam energy were in the range of 7–27nm and 23–29GPa, respectively. With an increase in the nitrogen ion beam concentration, the film surface roughness first decreased to a minimum value, and then increased, while the hardness first increased to a peak value, and then decreased. When the assisting ion beam energy and concentration were 300eV and 0.5, the SiCN film possessed the low surface roughness of 11nm and the highest hardness of 29GPa, its atoms ratio, C:Si:N:O was about 1:0.42:0.18:0.32. The bonding structure of the SiCN films mainly consisted of Si–C, Si–N, C–N, CN and CC bonds and corresponded to a network of the mixed sp2/sp3 hybridized bonds with the units of Si(C4), Si(N4) and Si(C4−nNn). The film mechanical properties were correlated to the proportion of Si–C, Si–N, CN and C–N bonds in the SiCN films.

XPS studies on silicon carbonitride films prepared by sequential implantation of nitrogen and carbon into silicon

Synthesis and Thermal Decomposition of Carbon Nitride Films Prepared by Nitrogen Ion Implantation into Graphite

Carbon Nitride Films Synthesized By Combined Ion-Beam And Laser-Ablation Processing

Ion beam synthesis of C-N crystalline film and its analysis

Spectra Characterization of Silicon Carbonitride Thin Films by Reactive Radio Frequency Sputtering

Electronic and Mechanical-Properties of Carbon Nitride Films Prepared by Laser-Ablation Graphite under Nitrogen Ion-Beam Bombardment

Study of the Growth of Thin Nitride Films under Low-Energy Nitrogen-Ion Bombardment

Thermal Nitridation Kinetics of Silicon Wafers in Nitrogen Atmosphere During Annealing

Structures and bonding properties of carbon nitride films prepared by radio frequency magnetron sputtering

Optical & Electronic Properties of Carbon Nitride Thin Films

Experimental Studies of Superhard Materials Carbon Nitride Cnx Prepared by Ion-Beam Synthesis Method

Surface Roughness, Mechanical Properties and Bonding Structure of Silicon Carbon Nitride Films Grown by Dual Ion Beam Sputtering

Synthesis of Carbon Nitride Films by Arc-Heated Atomic Nitrogen Beams Assisted Pulsed Laser Ablation

Formation of SiC-surface nanocrystals by ion implantation and electron beam rapid thermal annealing

Two-Phase Nanostructured Carbon Nitride Films Prepared by Direct Current Magnetron Sputtering and Thermal Annealing

Formation of SiC-surface layer by ion implantation

Ultrathin Nitride Films Grown under Low-Energy Ion Bombardment

Crystalline Carbon Nitride Films Prepared by Microwave Plasma Chemical Vapour Deposition

Synthesis of Crystalline Carbon Nitride by Microwave Plasma Chemical Vapor Deposition

Crystalline Carbon Nitride Film Synthesized by Ion Beam Assisted Magnetron Sputtering and Thermal Annealing in Nitrogen Gas

Carbon nitride films on diamond layers and their thermal behavior