Abstract:The influence of the nitrogen (N) content (0.0013-0.034 wt%) on the microstructures and 750 ?C tensile properties of a newly developed Ni-Fe based wrought superalloy (named as HT700T alloy) for ultra-supercritical power plant applications beyond 700 ?C was investigated using scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) techniques. The results show that the increase in the N content promotes the morphological transformation of the intergranular Cr23C6 carbides from semi-continuous rods to discrete granular particles, and leads to the decrease of the amount of the Cr23C6 carbides. Meanwhile, the increase in the N content promotes the formation of the MX phase and the MX phase more preferentially forms at the grain boundary. The N content has no obvious effects on the morphology of the gamma ' phase, but slightly decreases the gamma ' fraction. The average grain size continuously decreases with the increase of N content and the proportion of low Sigma coincident site lattice (CSL) boundary significantly increases at the 0.0077% N content. The 750 degrees C tensile properties show that the increase of N content has little effect on the yield and tensile strength of the alloy, while the ductility increases remarkably. A mixture fracture mode of intergranular and transgranular occurs in all samples regardless of the N content. The dominant deformation mechanism is gamma ' bypassing via Orowan looping regardless of the N content, while deformation microtwinning and stacking faults shearing the gamma ' precipitates are confirmed to be the assistant deformation mechanisms at the 0.0077% N content.

Isothermal decomposition behavior of the high nitrogen concentration γ-Fe[N] prepared from pure iron

In-situ Observation on the Isothermal Decomposition Process of Γ-Fe[n] by X-ray Diffraction

Microstructure and Characterization of High Hardness Produced in High-Nitrogen Austenite Intermediate Temperature Transformation

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Research on Mediate Temperature Decomposition of High Nitrogen Austenite

Initiatory Investigation on High-density Nano Precipitation of(非汉字符号) in Fe-N Austenite

An investigation on nitrogen uptake and microstructure of equimolar quaternary FeCoNiCr high entropy alloy after active-screen plasma nitriding

Homogenization of Nitrogen in Fe-3Si Alloy at High-Temperature Annealing Process

A Special Phase Transformation Phenomenon in High-Nitrogen Austenite

Isothermal transformation of high-nitrogen austenite

Studies on the Sample Preparation and Mediate Temperature Isothermal Tempering Process for Austenite with Homogeneous Nitrogen Content

PREPARATION AND PROPERTIES OF BULK AMORPHOUS Fe-Ni-P-B-Ga ALLOYS

Intermediate Temperature Transformation of the High-nitrogen Austenite

First-principles Study of the Effect of N on the ∑5 (210) [001] Grain Boundary of Γ-Fe

Preparation and properties of FeNiMnCuC0.2Alx high-entropy alloy

Morphology and Crystallographic Orientation Relationship in Isothermally Transformed Fe–N Austenite

Unusual Iron Nitride Formation Upon Nitriding Fe-Si Alloy

Preparation of Α′-Fe(n)/α′-fe8n by Γ′-Fe4n Precursor

Effects of Nitrogen Content on Microstructures and Tensile Properties of a New Ni–Fe Based Wrought Superalloy

Effects of Nitrogen in the (fe1−xnix)4n Compounds (0 ≤x ≤ 0.6)

Bainite Formation in a Carbon-Free Fe–Cr–N System