Abstract:The effect of nitrogen content on the formation of an equiaxed solidification structure of Fe-16Cr steel was investigated. Moreover, two different kinds of refractory materials, i.e., alumina and magnesia, were employed to control the type of oxide inclusion. The characteristics of TiN(-oxide) inclusions were quantitatively analyzed in both molten steel and solidified samples. When the melting was carried out in the alumina refractory, the grain size continuously decreased with increasing nitrogen content. However, a minimum grain size was observed at a specific nitrogen content (approx. 150 ppm) when the steel was melted in the magnesia refractory. Most of the single TiN particles had a cuboidal shape and fine irregularly shaped particles were located along the grain boundary due to the microsegregation of Ti at the grain boundary during solidification. The type of TiN-oxide hybrid inclusion was strongly affected by the refractory material where Al2O3-TiN and MgAl2O4-TiN hybrid-type inclusions were obtained in the alumina and magnesia refractory experiments, respectively. The formation of oxide inclusions was well predicted by thermochemical computations and it was commonly found that oxide particles were initially formed, followed by the nucleation and growth of TiN. When the nitrogen content increased, the number density of TiN linearly increased in the alumina refractory experiments. However, the number of TiN exhibits a maximum at about [N] = 150 ppm, at which a minimum grain size was obtained in the magnesia refractory experiments. Therefore, the larger the number density of TiN, the smaller the primary grain size after solidification. The number density of TiN in the steel melted in the magnesia refractory was greater than that in the steel melted in the alumina refractory at given Ti and N contents, which was due to the lower planar lattice disregistry of MgAl2O4-TiN interface rather than that of Al2O3-TiN interface. When ∆TTiN (= difference between the TiN precipitation temperature and the liquidus of the steel) was 20 K to 40 K, the number density of effective TiN was maximized and thus, the grain size was minimized after solidification. Finally, although most of the TiN particles were smaller than 1 μm in the molten steel samples irrespective of the nitrogen content, TiN particles larger than 10 μm were observed in the solidified samples when the nitrogen content was greater than 150 ppm. The growth of TiN particles during melting and solidification was well predicted by the combinatorial simulation of the ‘Ostwald ripening model’ based on the Lifshitz–Slyozov–Wagner theory in conjunction with the ‘Diffusion controlled model’ using Ohnaka’s microsegregation equation.

Unusual Iron Nitride Formation Upon Nitriding Fe-Si Alloy

Morphological and Dimensional Evolution of Nanosized Amorphous Silicon Nitride in α-Fe: Diffusional and Elastic Effects

Formation of iron nitride thin films with Al and Ti additives

Influence of Temperature on Phase Composition of Nitridation Products from Ferrosilicon Alloy

Preparation of Si3N4–TiN–SiC composite by partial substitution of Ti–Si–Fe alloy for Si under N2 atmosphere

Secondary Phases and Interfaces in a Nitrogen-Atmosphere Sintered Al Alloy: Transmission Electron Microscopy Evidence for the Formation of AlN During Liquid Phase Sintering

Isothermal decomposition behavior of the high nitrogen concentration γ-Fe[N] prepared from pure iron

Homogenization of Nitrogen in Fe-3Si Alloy at High-Temperature Annealing Process

Cost-effective manufacture and synthesis mechanism of ferrosilicon nitride porous ceramic with interlocking structure

Catalytic Nitridation Preparation of High-Performance Si3N4(w)-SiC Composite Using Fe2O3 Nano-Particle Catalyst: Experimental and DFT Studies

Graphite nucleation on (Al, Si, Mg)-nitrides: Elucidating the chemical interactions and turbostratic structures in spheroidal graphite cast irons

Anomalous grain growth in nanocrystalline Fe73.5Cu1Nb3Si13.5B9 alloys

Influence of sintering aids on the nitridation of reaction bonded Si 3N4/BN ceramics

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Nitridation Mechanism of Reaction Sintered Si3N4-SiC Composite

Synergistic Effect of Nitrogen and Refractory Material on TiN Formation and Equiaxed Grain Structure of Ferritic Stainless Steel

Effect of Si3N4 mesophase on the formation of Al2OC-AlNss in resin-bonded Al–Al2O3 composites

Liquid-Phase-Assisted Catalytic Nitridation of Silicon and In Situ Growth of α-Si3N4

Synthesis and magnetic properties of LaFe13--M Si N3 nitrides

Effect of Ti-Si-Fe alloy on the nitriding behavior of Si powder

An investigation on nitrogen uptake and microstructure of equimolar quaternary FeCoNiCr high entropy alloy after active-screen plasma nitriding