Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Influence of mechanical activation on combustion synthesis of fine silicon carbide (SiC) powder

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Combustion synthesis Si3N4 powders by using activation process

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Properties Of Mechanical Activation Combustion Synthesied High Alpha-Content Silicon Nitride Powders And Sintered Bulk Ceramics After Iteration Reactions

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

Characterization of mechanochemical modification in SiC powder

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Combustion synthesis of SiC/Al2O3 composite powders with SiC nanowires and their growth mechanism

Mechanical activation assisted combustion synthesis of AlN-Al2O3 composite ceramic powder

Controlled growth of SiC crystals in combustion synthesis

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Synthesis of Silicon Carbide Nanopowder Using Silica Fume

Preparation of SiC/Si3N4 composites with rod-like microstructure by combustion synthesis

Mechanical-activation-assisted combustion synthesis of α-SiAlON in air

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Synthesis of Mosi2/Wsi2 Nanocrystalline Powder by Mechanical-Assistant Combustion Synthesis Method

Preparation of porous silicon carbide by combustion synthesis