Comparing the tribological behavior of polycrystalline diamonds against steel GCr15 and ceramic Si 3 N 4 : friction and wear
xiwei cui,Yue Qin,Xin Han,Huanyi Chen,Xinxin Ruan,Hui Zhang,Chengcheng Jiao,Rongqi Mao,Jinglin Hao,Sizhuang Zhao,Shuai Hou,Xiaoxuan Pian,Yandong Wang,Kazuhito Nishimura,lifen deng,Nan Jiang
DOI: https://doi.org/10.2139/ssrn.4552304
IF: 3.806
2023-11-09
Diamond and Related Materials
Abstract:The tribological behaviors of polycrystalline diamonds (PCDs) against different materials is fundamental for their applications in abrasion and bearing industry. This paper systematically investigates the friction and wear of two types of PCDs: hot-filament-chemical-vapor-deposited (HFCVD) and high-pressure-high-temperature (HPHT) sintered, against steel GCr15 and ceramic Si 3 N 4 balls. It is found that firstly the coefficient of friction (COF) increased with the roughness increasing; Secondly both the COF and the wear rate (k) of ceramic Si 3 N 4 balls were generally lower than those of steel GCr15 balls, except for the HFCVD sample's COF; Thirdly the wear rate (k) increased with the PCD's grain size, accompanied by a decrease in residual cobalt content. The researchers observed transfer films of SiO 2 and its hydrate at the friction interface Si 3 N 4 /diamond, which were found to smoothen the friction and wear. Additionally, carbon-based transfer films were identified at both GCr15/PCD and Si 3 N 4 /PCD interfaces, mainly catalyzed by the residual cobalt in PCDs, leading to the phase transformation from sp 3 to sp 2 .
materials science, multidisciplinary,physics, applied, condensed matter, coatings & films