Abstract:Many metal materials possess the transition from strain localization to fracture, the so-called post-necking behavior, during large deformation under tensile load. It is crucial to understand and characterize the transition for the application of these materials. In this paper, the stress state dependence of the transition from strain localization to fracture of Ti–6.5Al–3.5Mo–1.5Zr–0.3Si alloy is characterized and analyzed by carrying out experiments and phase-field modeling. Firstly, tensile tests for smooth and notched round bars were conducted, in which the notched specimens have different notch radius. It was observed in the tests that the sharper the notch, the shorter the transition process, which can be explained as that high stress triaxiality would shorten the transition process. To further quantify the effects of stress triaxiality in the transition process, the phase-field fracture model involving the nucleation, growth and coalescence of micro-voids is developed to simulate and characterize the damage evolution observed in experiments. The simulations show that as the stress triaxiality increases, the material undergoes less plastic deformation, whether in the initiation of strain localization or the transition process. More interestingly, it is found that there exists a critical value of stress triaxiality, which can be considered the characteristic point of brittle-ductile transition. Above this point, the material has almost no plastic deformation before localization, and brittle fracture occurs directly. This work is meaningful for evaluating the safety of metal structures under complex loads.

Study of Plastic Hardening-Large Deformed Torsion Test and Simulation

Interpretation of Torsional Shear Results for Nonlinear Stress–strain Relationship

Experimental study on centrifuge concrete filled thin-walled steel tubular components under the action of torsion

EXPERIMENTAL STUDY ON CENTRIFUGAL CONCRETE-FILLED STEEL TUBES UNDER BENDING AND TORSION

Combination of Strength and Plasticity of a Low Alloy Steel after Torsional Prestrain

Thermomechanical Response of Commercially Pure Titanium under Large Plastic Deformation at High Strain Rates

A Tensile Characterization Study of Metal Sheet in Large-Strain

An experimental investigation of large-strain tensile behavior of a metal sheet

Research on the ductile fracture criterion in plastic deformation processes

Numerical simulation of CFRP strengthened steel square hollow section (SHS) subject to torsion

Strain Hardening under Large Deformation for AA5182

Constitutive Model for High Temperature Plastic Deformation of Low Carbon Steel

Extraordinary strain rate softening of metals in torsion

Numerical Simulation and Experimental Verification of Ductile Fracture Criteria of Metals

Large strain flow curve identification for sheet metals under complex stress states

Cyclic Deformation Behavior and Fatigue Crack Propagation of Low Carbon Steel Prestrained in Tension

Experimental and Theoretical Investigation of Size Effects on the Ductile/Brittle Fracture Toughness of A Pressure Steel

Constitutive Modeling for Large Deformation Behavior of Thermoplastic Olefin

Size Effect Studies on Tensile Tests for Hot Stamping Steel

Study of the Transition from Strain Localization to Fracture of Ti–6.5Al–3.5Mo–1.5Zr–0.3Si Alloy by Experiments and Phase-Field Modeling

Effects of the stress state on plastic deformation and ductile failure: Experiment and numerical simulation using a newly designed tension‐shear specimen