Abstract:The mechanical response and failure mechanism of commercially pure titanium subjected to combined tension-torsion loading are studied experimentally at strain rates ranging from 10−3 s−1 to 103 s−1. A novel tension-torsion split Hopkinson bar (TTHB) equipped with a high speed camera was utilised during high-rate experiments, while quasi-static tests were conducted using a universal screw-driven machine. The multiaxial dynamic experiments demonstrate the ability of the developed TTHB apparatus to achieve synchronisation of longitudinal and torsional waves upon loading the specimen, to satisfy the dynamic equilibrium of the specimen and to attain constant strain rate loading. The failure envelope of commercially pure titanium was analysed over a wide range of stress states including pure torsion, shear-dominated combined tension-shear, tension-dominated combined tension-shear, and plain tension. The analyses of the loading paths show that these were nearly proportional in terms of strain. The multiaxial failure stress locus was constructed in the normal versus shear stress space from experiments conducted at low and high rates of strain.The Drucker-Prager criterion was employed to approximate the failure envelope and to assess its rate sensitivity. The failure stress locus of commercially pure titanium and its rate dependence are reported for the first time. The TTHB apparatus developed allows the definition of the failure stress locus of aerospace materials directly from experiments and, therefore, the evaluation of the existing failure/yielding criteria.

Experimental Study on Tension Behavior of Pure Titanium at High Strain Rates

Experimental Study on Tensile Properties of CP-Ti Athigh Strain Rate and Different Temperatures

Effect of High Temperature Exposure and Strain Rate on Mechanical Properties of High-Strength Steel Rebars

Experimental Study on the Dynamic Tensile Behavior of A Poly-Crystal Pure Titanium at Elevated Temperatures

Experimental Study of Tensile Property of Cp-Ti at Intermediate Strain Rates

Strain-Rate-Dependent Tensile Response of Ti–5Al–2.5Sn Alloy

Dynamic Strain-Rate Effect On Uniaxial Tension Deformation Of Ti5al2.5sn Alpha-Titanium Alloy At Various Temperatures

Experimental analysis of the multiaxial failure stress locus of commercially pure titanium at low and high rates of strain

Research on stress relaxation behavior of TA15 titanium alloy

Temperature-Dependent Tension Plastic Deformation and Fracture Behavior of Ti-6.6Al-3.3Mo-1.8Zr-0.29Si Alloy at High Strain Rates

Strain Rate Sensitivity of Tensile Properties in Ti-6.6Al-3.3Mo-1.8Zr-0.29Si Alloy: Experiments and Constitutive Modeling

Thermomechanical Response of Commercially Pure Titanium under Large Plastic Deformation at High Strain Rates

Influences of temperature and strain rate on deformation twinning of polycrystalline titanium

Effect of Strain Rate on the Tension Behavior of Ti–6.6Al–3.3Mo–1.8Zr–0.29Si Alloy at Low Temperatures

Effect of Microstructure on High-Speed Tensile Mechanical Properties of Ti-1300 Alloy

The Constitutive Responses of Ti-6.6Al-3.3Mo-1.8Zr-0.29Si Alloy at High Strain Rates and Elevated Temperatures

Dynamic Deformation Behavior and Fracture Characteristics of a near α TA31 Titanium Alloy at High Strain Rates

High Strain-Rate Tensile Experiment on Polycarbonate Bar

Properties of Commercial Pure Titanium under Self-Heating and High-Pressure Heating Treatment

The Microstructures and Deformation Mechanism of Hetero-Structured Pure Ti under High Strain Rates

Tensile Behavior of Ti-5Al-2.5Sn Alloy at Low Temperatures and High Strain Rates