Abstract:Utilizing solid waste to produce foam material has become a significant direction in resource recycling. This study focuses solely on using silicomanganese slag and feldspar tailings as raw materials, utilizing a powder sintering process to produce autocatalytic foaming glass–ceramic foam. We formulated four mix ratios based on the compositional characteristics of the silicomanganese slag and feldspar tailings. The study then explored the evolution of phase formation and macroscopic pore morphology under varying preparation temperatures. Moreover, through multi-phase co-melting experiments, this work unveiled the high-temperature molten mass generation mechanism between silicomanganese slag and feldspar tailings. Our findings reveal that the glass melt generated from silicomanganese slag particles and the 'solid–liquid erosion behavior' of feldspar particles play pivotal roles in the formation of high-temperature co-melt substances. As the sintering temperature increases, the mixed powder exhibits three different states of high-temperature molten mass, which are the reasons for the evolution of the macroscopic pore structure. It is suggested that the addition of silicomanganese slag should be less than 50 %, and the heat treatment temperature should be below 1145 °C in preparing glass–ceramic foam with silicomanganese slag and feldspar tailings. The sample with 40 % silicomanganese slag and 60 % feldspar tailings, treated at 1140 °C, yielded glass–ceramic foam with a compressive strength of 1.68 MPa, apparent density of 0.279 g/cm 3 , porosity of 81.7 %, and thermal conductivity of 0.074 W·m −1 ·K −1 . In summary, this study provides a novel approach for the high-value utilization of silicomanganese slag and offers an economical route for developing lightweight, eco-friendly structural materials.

Fabrication of Clay Foam Ceramics Using Silicon Carbide and Ferric Oxide as Foaming Agents

Effect of Sic on Microstructures and Properties of Clay Foam Ceramics

Preparation of foam ceramics from solid wastes: a study on the relationship between firing regime and properties by grey system theory

Fabrication of Pure SiC Ceramic Foams Using SiO2 As a Foaming Agent Via High-Temperature Recrystallization

Recycling of Silicomanganese Slag and Fly Ash for Preparation of Environment-Friendly Foamed Ceramics

Preparation of ceramic foams from ceramic tile polishing waste and fly ash without added foaming agent

Effects of Foaming Agent on Microstructure and Properties of Porous Mullite Ceramics

PREPARATION AND MECHANICAL PROPERTIES OF FOAM GLASS-CERAMIC

Fabrication of SiC Foam Ceramics at a Low Sintering Temperature by Adding Fly Ash

Preparation and characterization of ceramic foams mainly containing extracted titanium residues and silica tailings

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

Preparation and physical properties of foamed ceramics from shale residue

Fabrication of Si 2 N 2 O Ceramic Foam by Combination of Direct Ink Writing and Biological Foaming Technique

Synthesis and properties of foam glass-ceramics from granite tailings by using SiC and MnO2 as the mixed foaming agent

Ultralight and Mechanically Robust SiC Foams with Interconnected Cellular Architecture

Fabrication and performance of SiO2-based electromagnetic wave penetrating foamed ceramics with dense surface

Foaming Mechanism and Performance of Closed–pore Foamed Ceramics Prepared Using Calcium Carbonate As a Foaming Agent

Effect of sintering temperatures and foaming agent content to the physical and structural properties of wollastonite based foam glass-ceramics

Preparation and characterization of foam ceramics from red mud and fly ash using sodium silicate as foaming agent

Effect of phase evolution and pyroplastic formation behavior on glass-ceramic foam derived from silicomanganese slag and feldspar tailings

Preparation of Glass-Ceramic Foams Using Extracted Titanium Tailing and Glass Waste As Raw Materials