Abstract:High-performance submicron ZrSiO4 powder is prepared by a sol-gel-microemulsion-hydrothermal method (S-G-M-H). In this method, the transformation from sol to gel is constrained in the droplets of the microemulsion and accelerated by the hydrothermal process. The interface change of sol/oil to gel/oil makes the emulsion automatic demulsificate without demulsiflers, which means that the organic solvents can be recycled. The preparation process is low-cost and environmentally friendly. The results show that the synthesized ZrSiO4 powder owns the optimized median diameter (D50) of 0.67 mu m under the optimized preparation condition of hydrothermal treatment at 150 degrees C for 7 h. The ZrSiO4 particles are the agglomeration of the primary particles with a size of about 100 nm. As an opacifler, 15 wt% submicron ZrSiO4 powder added give a whiteness value of 85 to the opaque glaze, which is significantly better than commercial ZrSiO4 powder with the same amount added. Meanwhile, the obtained submicron powder has excellent sintering activity. After sintered at 1300 degrees C for 2 h, the ZrSiO4 pellets has the density of 4.32 g cm(-3) and the porosity of 0.31%. (C) 2020 Elsevier B.V. All rights reserved.

Preparation of CaZr_4(PO_4)_6 powder by direct co-precipitation method

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of PbZrO3 Powder by a COprecipitation Method

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Synthesis and Densification of Nanometer K<sub>0.6</sub>Sr<sub>0.7</sub>Zr<sub>4</sub>P<sub>6</sub>O<sub>24</sub> Powder

Pva Assisted Synthesis of Nanosized Perovskite Pzt Powder by A Two-Stage Precipitation Route

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation of Zirconia Powders by Sol-gel Process

Low temperature synthesis of NaSICON NaZr2(PO4)3 powders with the assistance of in situ formed mineralizer

Preparation and Characterization of Pb(Zr0.52Ti0.48)O3 Ultrafine Powders by a Sol-Gel Combined with Combustion Process

Synthesis Of Perovskite Pb(Zr0.52ti0.48)O-3 (Pzt) Powders By A Modified Coprecipitation Method

Sintering, thermal expansion and mechanical properties of K0.6Sr0.7Zr4P6O24 ceramics

A Low Temperature Co-Precipitation Preparation of Nano-Sized Zinc Containing Β-Tricalcium Phosphate Powders

Synthesis of Perovskite Pb(Zr<sub>0.52</sub>Ti<sub>0.48</sub>)O<sub>3</sub> (PZT) Powders by a Modified Coprecipitation Method

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Coprecipitation Synthesis of MgO-Doped ZrO<sub>2</sub> Nano Powder

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Synthesis of perovskite Pb(Zr0.52Ti0.48)O3 (PZT) powders by a modified coprecipitation method

Synthesis of Perovskite Pb(Zr<sub>0.52</sub>Ti<sub>0.48</sub>)O<sub>3</sub> (PZT) Powders by a Modified Coprecipitation Method

Zirconia-Mullite Obtained from Co-Precipitated Zirconia-Mullite Composite Powders by Sps

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Preparation of CaZr_4(PO_4)_6 powder by direct co-precipitation method

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of PbZrO3 Powder by a COprecipitation Method

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Synthesis and Densification of Nanometer K<sub>0.6</sub>Sr<sub>0.7</sub>Zr<sub>4</sub>P<sub>6</sub>O<sub>24</sub> Powder

Pva Assisted Synthesis of Nanosized Perovskite Pzt Powder by A Two-Stage Precipitation Route

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation of Zirconia Powders by Sol-gel Process

Low temperature synthesis of NaSICON NaZr2(PO4)3 powders with the assistance of in situ formed mineralizer

Preparation and Characterization of Pb(Zr0.52Ti0.48)O3 Ultrafine Powders by a Sol-Gel Combined with Combustion Process

Synthesis Of Perovskite Pb(Zr0.52ti0.48)O-3 (Pzt) Powders By A Modified Coprecipitation Method

Sintering, thermal expansion and mechanical properties of K0.6Sr0.7Zr4P6O24 ceramics

A Low Temperature Co-Precipitation Preparation of Nano-Sized Zinc Containing Β-Tricalcium Phosphate Powders

Synthesis of Perovskite Pb(Zr<sub>0.52</sub>Ti<sub>0.48</sub>)O<sub>3</sub> (PZT) Powders by a Modified Coprecipitation Method

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Coprecipitation Synthesis of MgO-Doped ZrO<sub>2</sub> Nano Powder

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Synthesis of perovskite Pb(Zr0.52Ti0.48)O3 (PZT) powders by a modified coprecipitation method

Synthesis of Perovskite Pb(Zr&lt;sub&gt;0.52&lt;/sub&gt;Ti&lt;sub&gt;0.48&lt;/sub&gt;)O&lt;sub&gt;3&lt;/sub&gt; (PZT) Powders by a Modified Coprecipitation Method

Zirconia-Mullite Obtained from Co-Precipitated Zirconia-Mullite Composite Powders by Sps

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Synthesis of Perovskite Pb(Zr<sub>0.52</sub>Ti<sub>0.48</sub>)O<sub>3</sub> (PZT) Powders by a Modified Coprecipitation Method