Abstract:Tetragonal zirconia nanopowders (3Y-TZP NPs) stabilized by 3 mol % Y2O3 were synthesized by a novel sol–gel–flux method. The effects of calcination temperature, Y2O3 content, and molten salt system (NaCl + KCl binary system and NaCl unary system) on the phase composition and morphology of nanopowders (NPs) were investigated. Meanwhile, the sintering properties of the prepared 3Y-TZP NPs were studied. The 3Y-TZP NPs and sintered ceramics were characterized by thermogravimetry-differential scanning calorimetry (TG-DSC), X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), Brunauer–Emmett–Teller (BET) analysis, and X-ray fluorescence (XRF) spectroscopy. The results show that the optimum calcination temperature for obtaining dispersed ZrO2 NPs is reduced from 800 to 660 °C when the NaCl unary system is substituted by the NaCl + KCl binary system. 3Y-TZP NPs with a single tetragonal phase are obtained in the NaCl + KCl binary system when Y2O3 content in the raw material is 5 mol %. The average particle size of the obtained ZrO2 NPs is reduced from 47.25 nm in the unary system to 26.18 nm in the binary system because of the lower calcining temperature. Furthermore, the 3Y-TZP NPs obtained in the binary system have narrower particle size distribution and better sintering performance than ZrO2 NPs obtained in the unary system. After sintering for 4 h at 1200 °C, the former generated 3Y-TZP ceramics with higher density and finer grain size. This work produced narrow-distributed well-dispersed 3Y-TZP NPs with quasi-spherical morphology, which are good candidates for the applications, including oxygen sensors and thermal barrier coatings.

Synthesis and Densification of Nanometer K<sub>0.6</sub>Sr<sub>0.7</sub>Zr<sub>4</sub>P<sub>6</sub>O<sub>24</sub> Powder

Sintering, thermal expansion and mechanical properties of K0.6Sr0.7Zr4P6O24 ceramics

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation of CaZr_4(PO_4)_6 powder by direct co-precipitation method

Synthesis of Sr1+Xzr4p6-2xsi2xo24 Phosphate Powders by Solid State Reaction

Pva Assisted Synthesis of Nanosized Perovskite Pzt Powder by A Two-Stage Precipitation Route

Low temperature synthesis of NaSICON NaZr2(PO4)3 powders with the assistance of in situ formed mineralizer

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Coprecipitation Synthesis And Sintering Property Of (Ybxsm1-X)(2)Zr2o7 Ceramic Powders

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Research of ZrO2 Nano Powders Sintering Properties

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Sintering Properties of Tetragonal Zirconia Nanopowder Preparation of the NaCl + KCl Binary System by the Sol–Gel–Flux Method

Fabrication and sintering densification behavior of (Sr1-xPbx) TiO3 nano-powder

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Characterization and Synthesis of Pure Zro2 Nanopowders Via Sonochemical Method

Coprecipitation synthesis and sintering property of (Yb<SUB>x</SUB>Sm<SUB>1-x</SUB>)<SUB>2</SUB>Zr<SUB>2</SUB>O<SUB>7</SUB> ceramic powders

Microwave Assisted Sintering of Sr-doped Zinc Titanate (Sr0.2Zn0.8TiO3) Nano-ceramics

Synthesis and characterization of nanocrystalline PZT powders by a simple sol-gel method

Synthesis of Nanopowders of Ba(Ti0.8Zr0.2)O3

Preparation and Electronic Properties of Nanometer YSZ