Abstract:The fracture behavior of pipes with penetrating cracks was experimentally investigated with the results of the load-deflection curves and crack length. J-R curves were obtained from the testing results for different temperatures. With the decrement in temperature, the critical J integral decreases and the tearing modulus increases. An updated continuum damage model was proposed, in which the fracture energy density as a function of the stress triaxiality, temperature and strain rate in the transition region was taken as the critical damage factor. The uni-axial tension experiments at different temperatures were carried out to obtain the basic material properties and the critical fracture energy density, to verify the validity of the damage model. Based on detailed finite element analyses with the proposed updated continuum damage model, the loading level of pipes with penetrating cracks was estimated and compared with the experimental results, meanwhile the fracture processes of the pipeline structure in the ductile-brittle-transition-temperature region were reproduced. It has been shown that the fracture process in the transition region strongly depends on both the stress and strain state, and can be effectively predicted using the continuum damage models incorporating with the stress state effect.

Study of Dynamic Fracture Behavior of Pressure Pipes

Numerical Study of CFRP-Bonded Pressure Pipes Subject to Impact Load

A Numerical Study on the High-Velocity Impact Behavior of Pressure Pipes

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Analysis of Dynamic Fracture Mechanisms in Gas Pipelines

Burst Pressure of Pipelines with Plastic Anisotropy under Combined Internal and External Pressures

Theoretical Assessment of Burst Failure of Internally Pressurized Defect-Free Pipelines with Plastic Anisotropy

Dynamic Ductile Fracture Toughness Test and Numerical Simulation for Ultra-High Pressure Gas Pipelines

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Experimental and Fea Investigations on the Fracture Properties of Pipe Structures under Internal Pressure in Dbtt Region

Simulation and experimental verification on fluid-structure interaction of T-shaped pressure pipeline

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

Effect Of Pressure On Plastic Collapse Under The Combined Bending And Torsion Moments For Circumferentially Surface Flawed Pipes

Numerical Simulation and Safety Assessment Analysis for Pressure Pipe with Incomplete Penetration Defects

THE DEVELOPMENT AND APPLICATION OF THE DYNAMIC FRACTURE ANALYSIS CODE FOR CRACK PROPAGATION INGAS PIPELINES

Fracture Assessment of Dented Pipes with Cracks and Reliability-Based Calibration of Safety Factor

Study on Stress Intensity Factor of Girth Weld with Crack Defects

Consequence Analysis of Premixed Flammable Gas Explosion Occurring in Pipe Using a Coupled Fluid-Structure-fracture Approach

Dynamic Response of Pressurized Gas Pipes Subjected to Transverse Impact Loads

Fracture Response of Steel Pipelines under Combined Tension and Bending