Effect of Sr and Fe Doped LaCoO3 on Catalytic Oxidation of Soot and Sulfur Resistance
Wei Wei,Wu Ai-Chun,Qiao Zhi-Wei,Li Shu-Hua,Liang Hong,Peng Feng
DOI: https://doi.org/10.11862/CJIC.2020.031
2020-01-01
Chinese journal of inorganic chemistry
Abstract:A series of perovskite-type La1-xSrxCo1-yFeyO3 catalysts were successfully prepared by the citric acid-EDTA complexation. The catalysts exhibited excellent catalytic oxidation soot activity and sulfur resistance. The characterization of X-ray diffraction (XRD), fourier transform infrared spectra (FT-IR), scanning electron microscope (SEM), H-2-temperature-programmed reduction (H-2-TPR), X-ray photoelectron spectroscopy (XPS) and SO2-temperature programmed desorption (SO2-TPD) were used to reveal the effect of Sr and Fe doping on the physicochemical properties and sulfur tolerance of La1-xSrxCo1-yFeyO3 catalysts. Experimental results demonstrated that when the Sr doped with LaCoO3, it was beneficial for the catalyst to form more surface adsorption oxygen (O-2(-) or O-) and oxygen vacancies, thereby improving both the low-temperature redox ability and catalytic oxidation soot activity of catalyst. T-i (ignition temperature of soot) and T-m (complete conversion temperature of soot) are only 284 and 347 degrees C. Furthermore, with the doping of Fe, the low-temperature redox performance of catalyst was further improved, because the high-valent ions (Fe4+) were formed in the surface of catalyst, the Fe4+ ion could enhance the oxidation soot activity of catalyst. Moreover, the poisoning of SO2 was mainly attributed to the sulfation (SO32-, SO42-) of Co2+/Co3+ and surface adsorbed oxygen, leading to deactivating the active site (O-2(-) or O- and Fe4+) of catalyst. Simultaneous doping of Sr and Fe can form a strong interaction, which can effectively inhibit the deposition of sulfur species on the catalyst surface and reduce the poisoning of SO2 into the catalyst. Both XPS and SO2-TPD characterizations showed that the sulfur resistance of catalyst was mainly attributed the competitive adsorption of metal ions (Fe3+) on SO2, which could effectively reduce the poisoning of SO2 on the surface adsorption oxygen and Fe'. TPO (temperature programmed oxidation) activity characterization showed that LaSrCoFeO3-S still maintained good catalytic oxidation soot activity. T-i and T-m, were 320 and 361 degrees C, respectively, indicating that the simultaneous doping of Sr and Fe has excellent low-temperature catalytic soot activity and good sulfur poisoning ability.