Effects of the Co-Addition of Li, Sb, Ta on the Phase Structure and Piezoelectric Properties of (Na, K) NbO3 Lead Free Piezoceramics
Chu Xiangcheng,Gao Renlong,Huan Yu,Wang Xiaohui,Li Longtu
2013-01-01
Rare Metal Materials and Engineering
Abstract:Lead free (Na0.52K0.44Li0.04) (Nb1-x-ySbxTay)O-3(0<x, y<0.1) ceramics were synthesized by conventional solid process and pressureless sintering. The effects of the co-addition of LiSbO3-LiTaO3 on the microstructure, phase structure and piezoelectric properties of (K, Na)NbO3(KNN) ceramics were investigated. X-ray diffraction reveals that when y=0.04, the phase structure changed from orthorhombic to tetragonal symmetry with increasing content of Sb. When x=0.05, the phase structure remained tetragonal symmetry with increasing content of Ta. And in the latter composition region, the piezoelectric properties were enhanced well. The optimized properties were gained at x=0.05, y=0.06 with piezoelectric constant d33 similar to 334 pC/N, electromechanical coefficients of planar mode K(p similar to)0.35, dielectric constant similar to 4900, tan delta-0.027, P-r similar to 16.4 mu C/cm(2) and Ec similar to 8.4 kV/cm.