Structure and Electrical Properties of Lead-Free (Na0.5k0.5)nbo3-Batio3 Ceramics

YP Guo,K Kakimoto,H Ohsato
DOI: https://doi.org/10.1143/jjap.43.6662
IF: 1.5
2004-01-01
Japanese Journal of Applied Physics
Abstract:(Na0.5K0.5)NbO3 with 0–20 mol% BaTiO3 has been prepared following the conventional mixed oxide process. High-density samples were obtained through the addition of BaTiO3 into (Na0.5K0.5)NbO3 because of an increase in grain size. X-ray diffraction analysis revealed that, during sintering, all of the BaTiO3 diffuses into the lattice of (Na0.5K0.5)NbO3 to form a solid solution, in which orthorhombic symmetry changes to tetragonal symmetry at x≈0.06, and tetragonal symmetry changes to cubic symmetry at x=0.20 or higher. It was found that the samples with a low content of BaTiO3 exhibit relatively good ferroelectric and piezoelectric properties. For 0.98(Na0.5K0.5)NbO3-0.02 BaTiO3 ceramics, the remanent polarization (P r) is 7.5 µC/cm2 with a coercive field (E c) of 12 kV/cm. The piezoelectric constant d 33 reaches 104 pC/N. The electromechanical coupling coefficients of the planar mode k p and the thickness mode k t reach ∼29% and ∼38%, respectively. Our results show that (Na0.5K0.5)NbO3-BaTiO3 is a good lead-free piezoelectric ceramic.
What problem does this paper attempt to address?