Preparation and Properties of （Na0.50＋xk0.50-2Xlix）nb0.9ta0.1o3 Lead-Free Piezoelectric Ceramics by Sol-Gel Method

赵金秋,刘艳改,高广智,黄朝晖,房明浩

DOI: https://doi.org/10.14062/j.issn.0454-5648.2012.03.006

2012-01-01

Abstract:The ceramic powders,in which Li+ substituted(K0.5Na0.5)+ and Ta5+ substituted Nb5+,were prepared by a sol–gel method,and the(Na0.50+xK0.50–2xLix)Nb0.9Ta0.1O3(x = 0,0.02,0.04) ceramics were prepared via a pressureless sintering method.The effect of calcining temperature on the phase composition of ceramic powders was investigated.The influence of the Li+ substitution on the phase composition,microstructure,density and electrical properties of the ceramics was systematically analyzed.The results show that the optimal calcining temperature is 600 ℃.The analysis by transmission electron microscope indicated that the average size of the ceramic powders was 49 nm.The(Na0.50+xK0.50–2xLix)Nb0.9Ta0.1O3 ceramics had a single-phase perovskite structure with the or-thorhombic symmetry.The density of the(Na0.50+xK0.50–2xLix)Nb0.9Ta0.1O3 ceramics firstly increased and then decreased with the increase of Li+ content,while piezoelectric constant had the opposite transformation.The dielectric constant and remnant polarization were both improved when Li+ content was increased.When Li+ content was 0.04,the samples had an excellent piezoelectric constant(d33 = 94 pC/N),relative dielectric constant(er = 684.33) and remnant polarization(Pr = 98.27 μC/cm2).