Abstract:TiC bonded diamond composites were prepared from a mixture of Ti, graphite, and diamond powders as raw materials, with Si as sintering additives, through high-temperature and high-pressure (HTHP) technology. The reaction between Ti and graphite under 4.5–5 GPa pressure and 1.7–2.3 kW output power can produce TiC as the main phase. The diamond particles are surrounded by TiC, and the interface is firmly bonded. The coefficient of friction (COF) of TiC–diamond composites with POM and PP balls decreases with increasing load for a specific friction velocity. However, the COF of TiC–diamond composites with agate, Cu and Al balls increases with the rising load because of the enhanced adhesive wear effect. The COF of PP, Cu and Al balls slightly increases with the increase in friction velocity at a certain load. SEM results show that the surface of agate balls has rough, pear-shaped grooves and shallow scratches. The scratches on the surface of POM balls are wrinkled. The PP balls have pear-shaped groove scratches on their wear surfaces. The wear mechanism of TiC–diamond composites with Cu ball pairs is primarily adhesive wear. The abrasion of TiC–diamond composites with Cu ball pairs remains almost unchanged as the load increases. However, the depth and width of the pear-shaped grooves on the wear surface of TiC–diamond composites are significantly increased. This phenomenon may be attributed to the high rotational speed, which helps to remove the residual abrasive debris from the friction grooves. As a result, there is a decrease in both the depth and width of the pear-shaped grooves, leading to a smoother overall surface. The wear mechanism of TiC–diamond composites with Al ball pairs is abrasive wear, which increases with an increasing load. When the load is constant, as the speed increases, the wear morphology of TiC–diamond composites with Al ball pairs transitions from rough to smooth and then back to rough again. This phenomenon may be attributed to the wear mechanism at low speeds being groove wear and adhesive wear. As the speed increases, the wear particles are more easily removed from the wear track, leading to a reduction in abrasiveness. As the speed increases, the wear surface becomes roughened by a combination of grooves and dispersed wear debris. This can be attributed to the increased dynamic interaction between surfaces caused by higher speed, resulting in a combination of abrasive and adhesive wear. In addition, Cu and Al ball wear debris appeared as irregular particles that permeated and adhered to the surface of the TiC phase among the diamond particles. The results suggest that TiC–diamond composites are a very promising friction material.

Wear Properties of Cemented Carbides/cu-Based Alloy Composite Strengthening Materials for Milling Shoes

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Research On Wear Behavior Of Atc Cermet Material

Microstructure and wear resistance of bimodal cemented carbide coating prepared by direct laser powder deposition

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

Tribological and Electrochemical Corrosion Behaviors of Cu-based Powder Metallurgy Composites Reinforced by In-Situ WC with Different Morphology

Microstructure, mechanical and friction-wear properties of SiC-WC composite with Al and C as sintering aids

Spark Plasma Sintering Preparation of Tungsten Carbide-Reinforced Iron-Based Composite Materials: Wear Resistance Performance and Mechanism

Interface microstructure and abrasive wear properties of WC-iron matrix composites with Ni, Mo, Fe added to the preforms

Wear-Resistant TiC Strengthening CoCrNi-Based High-Entropy Alloy Composite

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Tribological properties and wear resistance mechanism of WC-ZrO2-Al2O3 ceramics

Microstructure and mechanical properties of WC–Co-based cemented carbide with bimodal WC grain size distribution

Effect of tungsten carbide content on the tribological behavior of TiB2–TiC-based cermets

Effect of Cu and CeO2 additives on structure and performance of WC-10Co cemented carbides

Influence of cutting parameters on PCD tool wear during milling tungsten carbide

Three-Body Abrasive Wear Behavior of WC-10Cr3C2-12Ni Coating for Ball Mill Liner Application

Investigation of abrasive wear resistance and wear mechanism of composite alloys

In Situ Synthesis and Tribological Characterization of TiC–Diamond Composites: Effect of the Counterface Material on Wear Rate and Mechanism

Effect of tool wear on machining quality in milling C f /SiC composites with PCD tool