Abstract:A method of preparation of prussian blue (PB) from a single ferricyanide solution and the mechanism of its formation are discussed. In a weak acidic medium (pH 3.6) of KH2PO4 (0.1 M)‐HCl, a thin film of PB is deposited on a gold electrode surface by using cyclic voltammetry between −0.2 and +0.6 V. It is confirmed that the coincident effect of the solution acidity on the PB preparation is exhibited by using either cathodical polarization or cyclic voltammetry. The UV‐vis absorption spectra from the various acidic solutions indicate that the absorption curve of pH at 3.6 is different from those of other pH values. Under the same conditions, PB cannot be deposited on a gold electrode surface from the ferrocyanide solution by using cyclic voltammetry and cathodical polarization. In addition, a kind of blue precipitate is gradually produced in the ferricyanide solution during standing after one day, and this is verified to be PB by the two pairs of its characteristic redox peaks at about +0.2 and +0.8 V vs. Ag/AgCl, which are obtained by immobilizing the blue precipitate mechanically on a gold electrode surface and recording the cyclic voltammogram while no similar precipitate occurs in the ferrocyanide solution during its standing course. Furthermore, the Fe2+ cannot be oxidized to Fe3+ on a gold electrode even when the positive potential reaches to +1.0 V, while Fe3+ can be easily reduced to Fe2+ at −0.2 V. It is concluded that the PB formation from the ferricyanide solution lies in the dissociation of ferricyanide ions.

Electrochemical deposition of Prussian blue on hydrogen terminated silicon(111)

Electroless metallization of hydrogen-terminated Si(100) surface functionalized by viologen

Electrochemical Deposition and Mechanism Investigation of Prussian Blue on Graphic Carbon Paste Electrode from an Acidic Ferricyanide Solution

Electrochemical Deposition of Prussian Blue from a Single Ferricyanide Solution

Functionalization of Hydrogen-Terminated Si(100) Substrate by Surface-Initiated Raft Polymerization of 4-Vinylbenzyl Chloride and Subsequent Derivatization for Photoinduced Metallization

Mechanism investigation of Prussian blue electrochemically deposited from a solution containing single component of ferricyanide

Electrochemical Behavior of Nanosized Prussian Blue Self-Assembled on Au Electrode Surface

Cold Deposition of Large-Area Amorphous Hydrogenated Silicon Films by Dielectric Barrier Discharge Chemical Vapor Deposition

Synthesis and Patterning of Prussian Blue Nanostructures on Silicon Wafer Via Galvanic Displacement Reaction

Photoelectric Properties Of Pbse/Baf2/Caf2 Films On Si(111)

Growth of Poly-Crystalline Si Films on Flexible Substrate by Hot Wire Chemical Vapor Deposition

Room Temperature Growth of Hydrogenated Amorphous Silicon Films by Dielectric Barrier Discharge Enhanced Cvd

Fabrication and electrochemical study of monodisperse and size controlled Prussian blue nanoparticles protected by biocompatible polymer

Growth of Si-C-H film by RF plasma enhanced chemical vapor deposition

Thin-Film Electrochemistry of Single Prussian Blue Nanoparticles Revealed by Surface Plasmon Resonance Microscopy.

Preparation and characterization of WTiO2 nanotubes decorated with Prussian blue nanoparticles and nanocubes with enhanced photoelectrochemical properties

Synthesis, Characterization, and Immobilization of Prussian Blue-Modified Au Nanoparticles: Application to Electrocatalytic Reduction of H2O2

Electrical and Optical Properties of Boron‐doped Nanocrystalline Silicon Films Deposited by PECVD

Photochemical Synthesis of Prussian Blue Film from an Acidic Ferricyanide Solution and Application

Morphology and Structure of Electrodeposited Prussian Blue and Prussian White Thin Films

Preparation of a PB@SiO 2 Photonic Crystal Composite with Enhanced Electrochromic Performance