Abstract:This work presents a photoinducedly electrochemical preparation of Prussian blue from a single sodium nitroprusside and insertion of cetyltrimethylammonium cations into Prussian blue as counter ions. The product of photoinducedly electrochemical reactions has a couple of voltammetric peaks at E degrees = 0.266 V in 0.2 mol l(-1) KCl solution, the measurements of X-ray powder diffraction and FT-IR spectroscopy show that it is Prussian blue (PB). The formation mechanism of a pre-photochemical reaction and subsequent electrochemical reaction is suggested. The cyclic voltammetric treatment of the freshly as-prepared PB film in 1.0 mmol l(-1) cetyltrimethylammonium (CTA) bromide solution leads to the insertion of cetyltrimethylammonium cations into the channels of Prussian blue, which substitutes for potassium ions as counter ions in Prussian blue. The Prussian blue containing CTA counter ions shows two couples of voltammetric peaks at E degrees = -0.106V and E degrees = 0.249 V in 0.2 mol l(-1) KCl solution containing 1.0 mmol l(-1) cetyltrimethylammonium bromide. Compared with the electrochemical behaviors of KFeFe(CN)(6) in 0.1 mol l(-1) KOH alkali solution, CTAFeFe(CN)(6) shows relatively durable voltammetric currents due to the hydrophobic effects of cetyltrimethylammonium. The diffusion coefficients for CTA and potassium cations were estimated to be D-CTA 1.25 x 10(-12) cm(2) s(-1). D-K 2.59 x 10(-12) cm(2) s(-1), respectively. The peak current of electro-catalytic oxidization on hydrogen peroxide showed a linear dependence from 6.59 x 10(-6) to 2.20 x 10(-4) mol l(-1) with R = 0.99947 (n=8). The linear regression equation was I-p (mA) = 0.82949 + 0.00594C (mu mol l(-1)) with errors of +/- 7.92833 x 10(-5) for the slope and +/- 0.01085 for the intercept with the detection limit of 1.46 x 10(-6) mol l(-1). Thus, it is expected to find its application in neutral or weak alkali medium for biosensors. (C) 2011 Elsevier Ltd. All rights reserved.

Electrochemical Deposition and Mechanism Investigation of Prussian Blue on Graphic Carbon Paste Electrode from an Acidic Ferricyanide Solution

Electrochemical Deposition of Prussian Blue from a Single Ferricyanide Solution

Mechanism investigation of Prussian blue electrochemically deposited from a solution containing single component of ferricyanide

Photochemical Synthesis of Prussian Blue Film from an Acidic Ferricyanide Solution and Application

Plasmonic Imaging Of Electrochemical Reactions At Individual Prussian Blue Nanoparticles

Determining the Electrochemical Activation Mechanism of Prussian Blue Analog Precatalysts for a High-Efficiency Oxygen Evolution Reaction

Electrochemical Behavior of Nanosized Prussian Blue Self-Assembled on Au Electrode Surface

Morphology and Structure of Electrodeposited Prussian Blue and Prussian White Thin Films

Thin-Film Electrochemistry of Single Prussian Blue Nanoparticles Revealed by Surface Plasmon Resonance Microscopy.

Renewable three-dimensional Prussian blue modified carbon ceramic electrode

Synthesis, Characterization, and Immobilization of Prussian Blue-Modified Au Nanoparticles: Application to Electrocatalytic Reduction of H2O2

Photoinducedly Electrochemical Preparation of Prussian Blue Film and Electrochemical Modification of the Film with Cetyltrimethylammonium Cation

The influence of deposition time on electrochemical performance of Prussian blue-modified submicron-structured gold electrodes for hydrogen peroxide sensing

Cathode/Anode Electrodes for Large-Area Bifunctional Electrochemical Devices Prepared by a Novel Na3Cit-assisted Chemical Deposition Method

Homogeneous and Nanogranular Prussian Blue to Enable Long-Term-Stable Electrochromic Devices

Optimized deposition time boosts the performance of Prussian blue modified nanoporous gold electrodes for hydrogen peroxide monitoring

Characterization of Prussian Blue Nanoparticles Prepared by Reverse Micelle and Electrochemical Study of Their Assembly

Electrochemistry And Electrocatalysis With Hemoglobin At Didodecyldimethylammonium Polyvinyl Sulfate (2c(12)N(+) Pvs-) Multibilayer Composite Film Electrodes

Synthesis and Characterization of Prussian Blue Modified Magnetite Nanoparticles and Its Application to the Electrocatalytic Reduction of H<sub>2</sub>O<sub>2</sub>

Improving the electrochromic performance of prussian blue (PB) thin films by using an innovative electrothermophoresis method

Unveiling the electrochromic mechanism of Prussian Blue by electronic transition analysis