Abstract:In this study, alumina–zirconia ceramics with ZrO 2 components obtained using different methods were investigated. Synthesized undoped ZrO 2 powder, commercial powder of ZrO 2 , doped with 3 mol% Y 2 O 3 and commercial powder of monocline zirconia doped with 2 mol% ceria were used. Highly dispersed (D50 < 100 nm) undoped zirconia was synthesized by precipitation from 1 M aqueous solution of ZrOCl 2 -8H 2 O with 25% aqueous ammonia solution. The resultant products were treated with water and isopropyl alcohol. Thermal treatment of the powder was carried out in a chamber furnace at a temperature beginning at 450 °C. Increasing the content of undoped ZrO 2 synthesized using the precipitation method increased the average size of ZrO 2 grains from 370 ± 20 nm to 560 ± 25 nm. During sintering of alumina-zirconia ceramics containing 20 vol% highly dispersed undoped zirconia, clusters of ZrO 2 particles unite to form large grains (800–1100 nm). Zirconia crystals with sizes less than 300 nm in the ceramic structure are observed inside and in the joints of Al 2 O 3 grains. With the increase in total undoped zirconia content from 10 to 20 vol% in alumina–zirconia ceramics, the proportion of t-ZrO 2 remaining during sintering decreases from 6 to 2 vol%. The introduction of cerium nitrate into a suspension of monoclinic zirconia at the stage of dispersion leads to the formation of ceramic CeAl 11 O 18 platelets with length of up to ~ 2 μm and width of ~ 0.15 μm. The bending strength is 800 ± 50 MPa and fracture toughness is 5.4 ± 0.7 MPa*m 1/2 in Al 2 O 3 –ZrO 2 ceramics containing 15 vol% zirconia doped with 2 mol% ceria.

Phase Stability and Thermal Expansion Property of ZrO2–NdO1.5–AlO1.5 Ceramics from 50 to 1550 °C

Thermal Stability of Bulk Zr2Al4C5 Ceramic at Elevated Temperatures

Phase evolution, thermophysical and mechanical properties of high-entropy (Ce0.2Nd0.2Sm0.2Eu0.2Yb0.2)2Zr2O7 ceramic for advanced thermal barrier coatings

Effect of thermal treatment at high temperature on phase stability and transformation of Yb2O3 and Y2O3 co-doped ZrO2 ceramics

Mechanical Properties Durability of Sc2O3-Y2O3 Co-Stabilized ZrO2 Thermal Barrier Materials for High Temperature Application

Preparation and High-Temperature Stability of (Zr1/5La1/5Sm1/5Dy1/5Gd1/5)O2−x High-Entropy Ceramic Materials

Mechanical and thermal properties of Al 2O 3-ZrO 2 composite ceramics at cryogenic temperatures

RETRACTED: Phase Transition and Thermal Expansion of the LaAlO3 Single Crystal at High Temperatures

The Effect of Al2O3 on the Thermal Stability and Mechanical Properties of 3Y-TZP

Resistance to Low‐Temperature Degradation of Equimolar YO1.5–TaO2.5 Stabilized Tetragonal ZrO2 Ceramics in Air

Structure Evolution and Electrical Properties of Y3+‐Doped Ba1−xCaxZr0.07Ti0.93O3 Ceramics

Brittle-to-Ductile Transition and High-Temperature Deformation in ZrO<SUB>2</SUB>(Y<SUB>2</SUB>O<SUB>3</SUB>) and Al<SUB>2</SUB>O<SUB>3</SUB> Ceramics as Evaluated by Small Punch Test

Role of t-ZrO2 stabilization methods in phase composition, structure and properties of ZTA ceramics

Influence of component manipulation on the structural, mechanical, thermophysical and electrical properties of La0·2Ce0.2Nd0.2(ZrxY1−x)0.4O2−δ high-entropy ceramics

Effect of Al2O3 on the Phase Stability of Y-Ce-TZP/Al2O3 Composites at Low Temperature

Phase Composition and Stability, Sintering and Thermal Conductivity of Gd2O3 and Yb2O3 Co-Doped YSZ

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Phase transformation of Y-Ce-TZP/Al2O3 composite ceramic annealed in air

Improving the Mechanical Properties and Microstructure of 12 mol% Ceria-Stabilized Tetragonal Zirconia Polycrystal Ceramics with Low-Content Nd2O3

Inhibited Grain Growth Through Phase Transition Modulation Enables Excellent Mechanical Properties in Oxide Ceramic Nanofibers up to 1700°C

Preparation and Thermophysical Properties of New Multi-Component Entropy-Stabilized Oxide Ceramics for Thermal Barrier Coatings