Abstract:Electrodeposited amorphous hydrated iridium oxide (IrOx) is a promising material for pH sensing due to its high sensitivity and the ease of fabrication. However, durability and variability continue to restrict the sensor's effectiveness. Variation in probe films can be seen in both performance and fabrication, but it has been found that performance variation can be controlled with potentiostatic conditioning (PC). To make proper use of this technique, the morphological and chemical changes affecting the conditioning process must be understood. Here, a thorough study of this material, after undergoing PC in a pH-sensing-relevant potential regime, was conducted by voltammetry, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Fitting of XPS data was performed, guided by raw trends in survey scans, core orbitals, and valence spectra, both XPS and UPS. The findings indicate that the PC process can repeatably control and conform performance and surface bonding to desired calibrations and distributions, respectively; PC was able to reduce sensitivity and offset ranges to as low as ±0.7 mV/pH and ±0.008 V, respectively, and repeat bonding distributions over ~2 months of sample preparation. Both Ir/O atomic ratios (shifting from 4:1 to over 4.5:1) and fitted components assigned hydroxide or oxide states based on the literature (low-voltage spectra being almost entirely with suggested hydroxide components, and high-voltage spectra almost entirely with suggested oxide components) trend across the polarization range. Self-consistent valence, core orbital, and survey quantitative trends point to a likely mechanism of ligand conversion from hydroxide to oxide, suggesting that the conditioning process enforces specific state mixtures that include both theoretical Ir(III) and Ir(IV) species, and raising the conditioning potential alters the surface species from an assumed mixture of Ir species to more oxidized Ir species.

Carbonate‐Melt Oxidized Iridium Wire for Ph Sensing

A pH Electrode Based on Melt-Oxidized Iridium Oxide

An Improved Method of Preparing Iridium Oxide Electrode Based on Carbonate-Melt Oxidation Mechanism

A long-term stable iridium oxide pH electrode

Effects of Structures on the Sensing Properties of Long-Term Stable IrOx Ph Electrodes

Electrochemical Sensor for Dissolved Carbon Dioxide Measurement

Experimental and Theoretical Constraints on Ph Measurements with an Iridium Oxide Electrode in Aqueous Fluids from 25 to 175 °C and 25 MPa

A New Electroplated Ir/Ir（OH） X Ph Electrode and Its Application in the Coastal Areas of Newport Harbor, California

Capillary Melt Method for Micro Antimony Oxide pH Electrode

An Antimony Oxide Ph Electrode for Tissue Culture Medium

Polarization Conforms Performance Variability in Amorphous Electrodeposited Iridium Oxide pH Sensors: A Thorough Surface Chemistry Investigation

Performance of IrOx Ph Sensor Prepared by Electrochemical and Thermal Oxidation

Effects of Thermal Oxidation Cycle Numbers and Hydration on Irox Ph Sensor

Insight into the Factors of Thermal Oxidation Influencing Properties of Iridium Oxide Electrodes

A Fabrication of Iridium Oxide Film Ph Micro-Sensor on Pt Ultramicroelectrode and Its Application on In-Situ Ph Distribution of 316L Stainless Steel Corrosion at Open Circuit Potential

Iridium Oxide Based Coaxial Ph Ultramicroelectrode

Nanochannel Templated Iridium Oxide Nanostructures for Wide-Range Ph Sensing from Solutions to Human Skin Surface.

A flexible IrO2 membrane for pH sensing

Fabrication and Characterization of Iridium Oxide pH Microelectrodes Based on Sputter Deposition Method

Development of SPEEK-Coated IrOx Sensor for High-Biomass Aquatic Ph Monitoring

Iridium Oxide Nanoparticles Modified Carbon Fiber Microelectrodes for Ph Detection