Synthesis and Magnetization Characteristics of Fe3O4 Nanoparticles
SHEN Yong-feng,ZHOU Fang,WANG Yan-dong,ZUO Liang
DOI: https://doi.org/10.3969/j.issn.1005-3026.2009.04.025
2009-01-01
Abstract:The effect of preparation process on the particle sizes and magnetization characteristics of Fe3O4 nanoparticles was characterized by XRD,high-energy XRD, TEM and vibrating sample magnetometer.It was indicated that the average particle size is 32 nm and 7 nm as the results of polyol method and co-precipitation process,respectively.The powdered Fe3O4 nanoparticle samples prepared by two methods showed that the saturated magnetization,remanent magnetization Mr,coercive force Hc are 6.8×10-3 A/m(8% lower than that of bulk samples),4.2×10-3 A/m,1.43×10-2 T and 3.3×10-4 A/m(about 96% lower than that of bulk samples),0.0 A/m,0.0 T,respectively.All these reveal that the size effect causes the occurrence of superparamagnetism,and that the particle size and magnetization characteristics of powdered Fe3O4 relate closely to its preparation process.