Abstract:Magnetite nanoparticles (Fe3O4) were prepared by chemical coprecipitation method using ferric chloride (FeCl3) and heptahydrate ferrous sulfate (FeSO4·7H2O) salts employing sodium hydroxide (NaOH) as a precipitant. To determine the size, shape, and chemical makeup of the produced magnetite nanoparticles, the generated powders were examined by transmission electron microscope, scanning electron microscope, atomic force microscope, and X-ray diffractometer. It was found that the magnetite powder had made a face-centered cubic crystal structure and spherical-like particle form with particle diameters of about 30 nm. The magnetic properties of magnetite nanoparticles were evaluated using a vibrating sample magnetometer. The obtained superparamagnetic properties of the produced nanoparticles, with saturation magnetization and coercivity of 50.75 emu/g and 30.09 Oe, respectively, allow them for applications in drug delivery, MRI contrast agent, catalysis, degradation of antibiotics, antibacterial activity, removal of heavy metals and organic dyes, etc.
What problem does this paper attempt to address?
This paper aims to solve the problems encountered in the synthesis process of iron oxide nanoparticles (especially magnetite nanoparticles Fe₃O₄), including how to use iron salts as precursors in aqueous solutions to prepare high - quality magnetite nanoparticles by the co - precipitation method. Specifically, the research focuses on the following aspects:
1. **Improving the quality of nanoparticles**: The research controls the size, shape and composition of nanoparticles by optimizing synthesis conditions, such as reaction temperature, pH value, ionic strength, and the properties of alkaline solutions, thereby improving the quality and purity of nanoparticles.
2. **Achieving large - scale production**: The research explores a simple and easy - to - scale - up synthesis method to meet the demand for a large number of high - quality nanoparticles in industrial applications, especially in the fields of drug delivery, MRI contrast agents, catalysis, antibiotic degradation, antibacterial activity, heavy metal and organic dye removal.
3. **Characterizing the properties of nanoparticles**: The crystal structure, morphology, magnetism and thermal stability of the prepared magnetite nanoparticles are comprehensively characterized by a variety of technical means (such as X - ray diffractometer (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), atomic force microscope (AFM), vibrating sample magnetometer (VSM) and thermogravimetric - differential thermal analysis (TG - DTA)).
In summary, the main purpose of this paper is to develop an efficient and scalable method for preparing high - quality magnetite nanoparticles through optimizing synthesis conditions and characterization techniques, and to explore their potential applications in multiple fields.