Abstract:The ultrasonic electroless Ni-P plating is fabricated on the TC4 titanium alloy pretreated by zinc double immersion and alkaline pre-plating, and then is carried out heat-treatment at different temperature. The effects of heat-treatment on the microstructure and phase structure of the ultrasonic electroless Ni-P plating and their tribological behavior are investigated by SEM/EDS, XRD, a Vikers indenter, and a pin-on-disk wear testing machine. It is observed that the morphology of the ultrasonic electroless Ni-P plating has the typical cauliflower-like nodular structure and the average size of nodular is approximately 7 μm. EDS studies suggest that the phosphorous content of the plating is as high as 11 at%. The ultrasonic electroless Ni-P plating exhibits obvious amorphous structure characteristics by XRD analyzers. After heat-treatment at 400 °C, the structure of the ultrasonic electroless Ni-P plating changes from amorphous to crystalline state, and the interface of the nodular structure becomes clear and the nodular size is refined. It is because the dispersed Ni 3 P second-phase particles are uniformly and continuously distributed in the nickel solid solution. Compared with the TC4 substrate, the microhardness and the wear resistance of the ultrasonic electroless Ni-P plating are greatly improved, especially for the heat-treatment at 500 °C. The wear mechanism of the TC4 substrate is severe adhesion and abrasion wear, with slight oxidation wear, while the ultrasonic electroless Ni-P plating shows plastic deformation and microabrasion wear. After heat-treatment, the wear mechanism of the ultrasonic electroless Ni-P plating is slight abrasion wear.

Preparation and Characterization of Ni-Coated Cr3c2 Powder by Room Temperature Ultrasonic-Assisted Electroless Plating

Preparation of Nickel-Coated Tungsten Carbide Powders by Room Temperature Ultrasonic-Assisted Electroless Plating

Study on Microstructure and Properties of FeNiCr/Ni Coated Cr_3C_2 Coatings Deposited by High Velocity Arc Spraying

A Specific Chemical Activation Pretreatment for Electroless Nickel Plating on SiC Ceramic Powders

Preparation of Ni-Coated SiC Ceramic Composite Powder by Electroless Plating

Co–Al2O3 nanocomposites powder prepared by electroless plating

Electroless Co-P Alloy Plating of Superfine Si3N4 Powders

Exploration of electrodeposited process of Ni-Co-Cr coating and investigation of Cr doping strengthening mechanism by indentation simulation

Preparation and Characteristics of New Type Nanocomposite Powder

Preparation and characterisation of the Ni-C composite coating electrodeposited with carbon sol

Preparation of Cr Hard Coatings by Ion Beam Assisted Electron Beam Vapor Deposition on Ni and Cu Substrates

Preparation of compound powder of Nickel-coated copper with chemical plating process

Ni-Ce-P Electroless Plating and Properties of the Coating on 27simn Steel

Electrochemical co-deposition of carbon nanotube/Ni composite layer

Enhancement of Corrosion and Wear Resistance of Ni-P Coatings Stems from the Synergistic Effects of Cr3C2 and Heat Treatment

Study of properties of Ni-base nano-ZrO2 composite plating coatings

PREPARATION OF ULTRAFINE W–Cu COMPOSITE POWDER USING ULTRASONIC-ASSISTED ELECTROLESS PLATING

The Microstructure and Tribological Behavior of Ultrasonic Electroless Ni-P Plating on TC4 Titanium Alloy with Heat-Treatment

Preparation of thin solid CoNiFe films by pulse-reverse electroplating technique

The Relation of Formation Mechanism, Microstructural Evolution and Mechanical Properties of Ni-based Coatings Produced via High Pressure Cold Spray Deposition

Study on Properties of Double-Layered Ni–P–Cr Composite Coating Prepared by the Combination of Electroless Plating and Pack Cementation