Study of properties of Ni-base nano-ZrO2 composite plating coatings

Lei Zhang,BenLiang Sun,Lin Wang,Yang Xu,Yang Li,Xin Shen

DOI: https://doi.org/10.4028/www.scientific.net/AMR.239-242.1452

2011-01-01

Abstract:The surface of copper plate of the mold need to be reinforced to obtain the plating coatings with high hardness and corrosion resistant properties. Nowadays, Ni-base alloy coatings is used widely in the industrial production. In order to raise the service life of mold, the experiments on the property of Ni-base nano ZrO2 composite plating coatings was done in this paper. The experiments were planned with the orthogonal test design method. The effective factors on the property of coatings, bath temperature, cathode current density, the distance between two electrodes and the magnitude of Nano-ZrO2,were experimentally studied. The optimum process parameter were obtained. The results show that the composite plating layer of Ni-base Nano ZrO2 with good properties can be obtained. The optimal conditions are as follows: the bath temperature is 40 degrees C, cathode current density is 3A/dm(2), the distance between two electrodes is 12 cm, the magnitude of Nano-ZrO2 is 12g/L. In addition binding strength of the coatings were measured quantitatively, and the structure of the plating layer were observed with SEM. The layer with good properties can be obtained in this method.