Abstract:In this paper, the effect of internal curing with pre-soaked lightweight aggregate (PSLWA) on shrinkage and interior relative humidity of four series concretes with compressive strength at 28 days around 30MPa, 60MP, 90MPa and 100MPa is investigated. The shrinkage induced cracking performance of concretes is evaluated with concrete-steel composite ring tests. The results show that the development of the internal relative humidity of concrete since casting exhibits first a vapor saturated stage (RH=100%, stage I), followed by gradually reducing stage (RH<100%, stage II). Under sealing, internal relative humidity at the center of the specimen for a given age is obviously decreased with increase of concrete strength. Under drying, similar internal relative humidity value is observed at 28 days for all concretes without internal curing. As PSLWA was added, the reduction rate on interior humidity in stage II is significantly decreased. But the efficiency on internal humidity rising is greatly influenced by concrete strength. The autogenous shrinkage is increased with increase of concrete strength. The drying shrinkage is decreased with increase of concrete strength. The total shrinkage of concrete is increased with increase of concrete strength. As PSLWA was added, the shrinkage reduction in both autogenous and drying shrinkages is obviously in high strength concretes, such as 90MPa and 100MPa concretes. The shrinkage reduction of internal curing on relatively low strength concrete, such 30MPa and 60MPa concrete is not obvious. Internal curing with PSLWA can greatly improve the shrinkage induced cracking performance. All concrete rings without internal curing are cracked under drying. The compressive strain in the steel ring at the concrete ring cracking is about 75 to 101 mu m/m. By contrast, the stable compressive strain at the inner steel ring for the concretes with internal curing becomes 10 to 40 mu m/m and no visible cracks were found on the specimens.

RELATIONSHIP BETWEEN DRYING SHRINKAGE AND RELATIVE HUMIDITY OF CONCRETE

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Identification of Indexes That Could Reflect Early Drying Shrinkage of High Strength Concrete with Minerals

Shrinkage And Interior Humidity Of Concrete Under Dry-Wet Cycles

Influence of Shrinkage Retarder on Early Self-Shrinking of Concrete

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Tests and Simulations of Interior Humidity and Shrinkage of Concrete under Sealed Condition

Experimental Study on the Internal Relative Humidity in Concrete under Dry-Wet Cycles

Experimental Study on Relationship Between Shrinkage Strain and Environmental Humidity of Concrete

Integrative Studies on Autogenous and Drying Shrinkages of Concrete at Early-Age

Uniform driving force for autogenous and drying shrinkage of concrete

Influence of Relative Humidity on Shrinkage of Mortar and Concrete

Drying Shrinkage-Induced Cracking Resistance of Non-Ballast Track Slab Concrete

Interior Relative Humidity of Normal- and High-Strength Concrete at Early Age

Influence of Fly Ash on the Deformation of Shrinkage-compensating Concrete with the Same Level of Strength

Effects of water-binder ratio and coarse aggregate content on interior humidity, autogenous shrinkage, and drying shrinkage of concrete

The Research of the Effect of Fly Ash on the Shrinkage Property of Commercial Concrete

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Autogenous Shrinkage Measuring of Concrete and Model Analysis

Evaluation of Shrinkage Induced Cracking in Concrete with Impact of Internal Curing and Water to Cement Ratio

Calculation of Shrinkage Stress in Concrete Structures with Impact of Internal Curing