Abstract:In this paper, the effect of internal curing with pre-soaked lightweight aggregate (PSLWA) on shrinkage and interior relative humidity of four series concretes with compressive strength at 28 days around 30MPa, 60MP, 90MPa and 100MPa is investigated. The shrinkage induced cracking performance of concretes is evaluated with concrete-steel composite ring tests. The results show that the development of the internal relative humidity of concrete since casting exhibits first a vapor saturated stage (RH=100%, stage I), followed by gradually reducing stage (RH<100%, stage II). Under sealing, internal relative humidity at the center of the specimen for a given age is obviously decreased with increase of concrete strength. Under drying, similar internal relative humidity value is observed at 28 days for all concretes without internal curing. As PSLWA was added, the reduction rate on interior humidity in stage II is significantly decreased. But the efficiency on internal humidity rising is greatly influenced by concrete strength. The autogenous shrinkage is increased with increase of concrete strength. The drying shrinkage is decreased with increase of concrete strength. The total shrinkage of concrete is increased with increase of concrete strength. As PSLWA was added, the shrinkage reduction in both autogenous and drying shrinkages is obviously in high strength concretes, such as 90MPa and 100MPa concretes. The shrinkage reduction of internal curing on relatively low strength concrete, such 30MPa and 60MPa concrete is not obvious. Internal curing with PSLWA can greatly improve the shrinkage induced cracking performance. All concrete rings without internal curing are cracked under drying. The compressive strain in the steel ring at the concrete ring cracking is about 75 to 101 mu m/m. By contrast, the stable compressive strain at the inner steel ring for the concretes with internal curing becomes 10 to 40 mu m/m and no visible cracks were found on the specimens.

Effects of water-binder ratio and coarse aggregate content on interior humidity, autogenous shrinkage, and drying shrinkage of concrete

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Integrative Study on the Effect of Internal Curing on Autogenous and Drying Shrinkage of High-Strength Concrete

Tests and Simulations of Interior Humidity and Shrinkage of Concrete under Sealed Condition

Integrative Studies on Autogenous and Drying Shrinkages of Concrete at Early-Age

Uniform driving force for autogenous and drying shrinkage of concrete

Tests and Simulations on Shrinkage of Concrete at Early-Age

Shrinkage of High-Strength Calcium Sulfoaluminate Cement Concrete with Impact of Pre-Soaked Lightweight Aggregate Internal Curing

Influence of Pre-wetted Lightweight Aggregate on Early-age Shrinkage of High Strength Concrete

Evaluation of Shrinkage Induced Cracking in Concrete with Impact of Internal Curing and Water to Cement Ratio

Integrated Shrinkage, Relative Humidity, Strength Development, and Cracking Potential of Internally Cured Concrete Exposed to Different Drying Conditions

Autogenous Shrinkage Measuring of Concrete and Model Analysis

Combination Effects of Internal Curing and Permanent Formwork on Shrinkage of High Strength Concrete

Influence of Shrinkage Retarder on Early Self-Shrinking of Concrete

Understanding Restraint Effect of Coarse Aggregate on the Drying Shrinkage of Self-Compacting Concrete

Shrinkage And Interior Humidity Of Concrete Under Dry-Wet Cycles

Experimental and Theoretical Studies on Autogenous Shrinkage of Concrete at Early Ages

Influence of Superplasticizer and Shrinkage-Reducing Admixtures on Early Age Shrinkage of Concrete

Shrinkage-reducing effect and strength development of internally cured concrete under different curing conditions

THE AUTOGENOUS SHRINKAGE OF CONCRETES PREPARED WITH THE BINDERS CONTAINING DIFFERENT KINDS OF MINERAL ADMIXTURE

Influences of Water-binder Ratio and Dosage of Fly Ash on Autogeneous Shrinkage of Shrinkage-Compensating Concrete