Abstract:Titanium nitride (TiN) film was deposited on 304 stainless steel using a hollow cathode discharge ion-plating (HCD-IP) technique. Film thickness and N/Ti ratio were controlled. The depth profile of the composition was determined by secondary ion spectroscopy (SIMS). The results showed that the compositions of the films were uniform for the films deposited at the same deposition conditions. The purpose of this study is to investigate the variation of structure and mechanical properties of the TiN films with different film thickness. The preferred orientations of TiN films were determined using X-ray diffraction (XRD). The dominant preferred orientation of the TiN coatings for the deposition conditions was (111), especially for the films thicker than 1 μm. The residual stress of the TiN films was also measured by XRD using sin2 Ψ method. The residual stress was ranging from −5.93 to −2.70 GPa, varying with film thickness. Hardness of the films was measured by nanoindentation. The hardness values were ranging from 14.9 to 33.6 GPa, increasing with the film thickness. The ultimate interfacial shear stress between TiN/304SS was determined by in-situ strip tension of the TiN-coated specimens in a scanning electron microscope (SEM) chamber. The limiting thickness for the effective measurement of interfacial shear strength by the in-situ strip tension method is close to 0.5 μm. N/Ti ratios of the thin films were all at 0.8 measured using both X-ray photoelectron spectrometer (XPS) and Rutherford backscattering spectrometer (RBS). The packing factors of TiN films, calculated from the results of RBS, were 0.62–0.99, increasing with film thickness and leveling off at a thickness above 1.2 μm.

Nanocrystalline Titanium Nitride Films Prepared by Electrophoretic Deposition

Electrophoretic Deposition of Nacre Coatings on Titanium Substrates

Study of optical and electrical properties of TiN thin films prepared by cathodic ion sputtering

Formation Of Nanocrystalline Tin Film By Ion-Beam-Enhanced Deposition

Composition and Texture of TiN Thin Films Fabricated by ECR Enhanced Sputtering Deposition

Structural and Hydrophilic Properties of TiN Films Prepared by Ultrasonic Atomization Assisted Spray Method under Low Temperature

Study of Titanium Nitride for Low-E Coating Application

TiN/AlN Nano Multilayers Film Fabricated by Plasma Enhanced Atomic Layer Deposition

Influence of Deposition Time on Titanium Nitride (TiN) Thin Film Coating Synthesis Using Chemical Vapour Deposition

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Microstructural and Electrical Resistivity of TiN Electrode Films Prepared by Direct Current (DC) Reactive Magnetron Sputtering

Low Temperature Deposition of TiN Using Tetrakis(dimethylamido)‐Titanium in an Electron Cyclotron Resonance Plasma Process

EFFECT OF SPRAYING DISTANCE ON THE PROPERTIES OF TITANIUM NITRIDE FILMS PREPARED BY ATMOSPHERIC PRESSURE CHEMICAL VAPOR DEPOSITION

Properties and morphology of TiN films deposited by atomic layer deposition

TiNx Thin Films for Energy-Saving Application Prepared by Atmospheric Pressure Chemical Vapor Deposition

Nanohardness of nanocrystalline TiN thin films

Deposition of Polymers on Titanium Nitride Electrodes

AFM Study on the Surface Morphologies of TiN Films Prepared by Magnetron Sputtering and Al2O3 Films Prepared by Atomic Layer Deposition

Mechanical properties of TiN thin film coatings on 304 stainless steel substrates

Plasma Spray Deposition Enhancement of Titanium Nitride Layer Using Nitrogen-Contained Plasma Irradiation of Titanium Substrate as a Pre-spraying Method

Room Temperature Deposition of Titanium Carbide Thin Films Using Dense Plasma Focus Device