Effects of powder microstructure on the critical current density of Ag-sheathed BPSCCO superconducting tapes

Yanwei Ma,Haozhuan Lin,Zutang Wang
DOI: https://doi.org/10.1016/0167-577X(95)00220-0
IF: 3
1996-01-01
Materials Letters
Abstract:The effects of powder microstructure on the critical current density of Ag-sheathed BPSCCO superconducting tapes have been studied. Two kinds of tapes were fabricated by the powder-in-tube technique using powders A and B, respectively; subsequent processing technique and heat treatment were under the same condition. The Jc of the tapes made from powder A was between 1.8 × 104 and 2.3 × 104 A/cm2 at 77 K, 0 T, while the Jc of the samples prepared from powder B ranged from 0.7 × 104 to 0.1 × 104 A/cm2. A detailed investigation of the starting powder and tapes has been carried out by means of X-ray diffraction, SEM and density measurement. It has been found that the difference between the two kinds of tapes is attributed to the different powder microstructures. The optimum powder microstructure is a large plate-like 2212 phase together with a small quantity of 2223 and non-superconducting phases.
What problem does this paper attempt to address?