The oxide-layer configuration alteration and pseudo-ductile crack propagation mechanisms in composites induced by different relative thicknesses of CVI HfC-SiC multiphase matrix
Xinhao Shi,Tao Feng,Wanbo Hou,Jiahui Ding,Xianglei Liu,Hongjiao Lin,Mingde Tong
DOI: https://doi.org/10.1016/j.compositesb.2023.111012
IF: 11.322
2023-09-22
Composites Part B Engineering
Abstract:Carbon fiber-reinforced HfC-SiC ceramic matrix composites (C f /HfC-SiC) with different HfC-SiC matrix thicknesses were prepared by the chemical vapor infiltration method. The microstructure, ablation, and pseudo-ductile fracture behaviors of the composites were studied. The results proved that with the change of the HfC-SiC layer relative thickness, the oxide-layer configuration changed to promote its densification, which improved the ablative protection and mechanical properties of C f /HfC-SiC composites. After ablation, when the relative volume proportion of the HfC-SiC matrix was the utmost (24.7/15.5), the composites had the best ablation resistance due to the tubular lamination configuration HfO 2 layer. This caused the composite to have the highest residual bending strength (215.8MPa) and strength retention rate (79.7%). In addition, a pseudo-ductile crack propagation model was established to determine the influence of the induction of residual stress and the relative HfC-SiC layer thickness on the fracture behavior in the composites. Results suggested that in the real crack deflection mechanism, due to the induction of residual stress, the stress state in the HfC-SiC matrix with the increase of the HfC layer thickness changed to form more ring deflection cracks at the HfC/SiC interface. It provides a way to study the pseudo-ductility behavior of multiphase matrix composites and explain the improvement of its predictability and failure.
engineering, multidisciplinary,materials science, composites