Effects of PES support layer structure on pervaporation performances of PDMS/PES hollow fiber composite membranes
de sun,qingchun yang,hualong sun,jiaming liu,zilong xing,bingbing li
DOI: https://doi.org/10.1080/19443994.2015.1028458
IF: 1.1
2016-01-01
Desalination and Water Treatment
Abstract:Polyethersulfone (PES) hollow fiber ultrafiltration (UF) membranes were fabricated by the dry/wet-spinning method; hydrophobic PDMS/PES composite membranes which were supported by self-prepared PES hollow fiber UF membranes were prepared for the pervaporation (PV) separation of ethanol from water. Impacts of PES support layer on the PV performances of PDMS/PES composite membranes were studied. Experimental results showed that, while working as a support to PDMS active layer, PES hollow fiber membrane could affect the PV performance of PDMS/PES membranes greatly. Pervaporation performance of the membrane which its PES support layer had bigger porosity and bigger mean pore size was apparently superior to that of the membrane which its PES support layer had smaller porosity and smaller mean pore size. After being treated with ethanol and hexane, PES membrane was dried in air for 20min before being immersed in PDMS coating solution; the prepared PDMS/PES membrane had the best PV performance with a permeate flux of 330g/(m(2)h) and a separation factor of 5.8. Effects of process parameters, such as feed temperature, permeate pressure, and feed flow rate, on membrane properties were investigated. For the separation of a 5wt.% ethanol-water mixture, with an increase in feed temperature from 30 to 60 degrees C, water flux and ethanol flux increased from 51 to 328g/(m(2)h) and from 14 to 88g/(m(2)h), respectively; the variation of permeation flux followed the Arrhenius relationship and the activation energy values for water and ethanol were 54.54 and 53.44 kJ/mol, respectively; separation factor varied from 5.1 to 6.0. When the feed temperature was 50 degrees C and feed concentration was 5wt.%, with an increase in permeate-side pressure from 1 to 40mmHg, water flux dropped sharply from 334 to 14g/(m(2)h) and ethanol flux dropped moderately from 82 to 22g/(m(2)h), and as a result, separation factor increased. With the increase in feed flow rate from 0.1 to 10L/min, both flux and separation factor increased rapidly at first and then leveled off at 2L/min for the reason of concentration polarization.