Abstract:Based on the Lcr wave acoustoelastic effect, surface stress of laser cladding Fe314 alloy coating after ultrasonic impact treat (UIT) was measured, and relation between Lcr wave acoustoelastic coefficient and repetition rate of UIT was discussed in this paper. The laser cladding Fe314 alloy coating was prepared on surface of carbon steel and impacted with different repetition rates of UIT by using UIT-300 system. After that, the experimental system of stress measurement with Lcr wave, consisting of a ultrasonic wave generator, a digital oscilloscope and two Lcr wave transducers (including one transmitting transducer and one receiving transducer) with 2.5MHz frequency, was used to collect Lcr waves of coating with calibration test, and then the difference in time of flight between Lcr waves was calculated with the cross correlation theory. To explain experimental results, the microstructure and three dimensional surface topography of coating were observed by using SEM and LSCM. Results show that as repetition rate of UIT increases, the Lcr wave acoustoelastic coefficient increases, when it reaches 300%, the Lcr wave acoustoelastic coefficient also reaches the maximum, after that the Lcr wave acoustoelastic coefficient decreases irregularly as repetition rates of UIT increases further. Compared with the Lcr wave acoustoelastic theory, when stress is in the range of turning point stress, there is a deviation on experimental result, and that deviation becomes more obvious as stress and repetition rate of UIT increase. It is analyzed that the change of microstructure, deformation state and initial stress of coating caused by UIT and different repetition rate are main reasons.

Measurement of Residual Stress in Multitrack Laser-Clad Coating

Study on Measurement Method of Interior Stress Distributions in Engineering Rolled-Plates

Depth-sensing Indentation Measurement and Finite Element Analysis of Residual Stress Field Near Fatigue Crack Tip

Progress and Challenges of Ultrasonic Testing for Stress in Remanufacturing Laser Cladding Coating

Research on Welding Residual Stress Measurement Using Electromagnetic Acoustic Transducer

OS13F106 Progress of the Residual Stress Measuring Techniques of Thermal Barrier Coatings

Numerical research on effect of overlap ratio on thermal-stress behaviors of the high-speed laser cladding coating*

FIB-DIC ring-core measurement of the residual stress on HiPIMS W/Cu and Cr/Cu multilayer thin films

Residual Stress Measurement of Thermal Barrier Coatings

Effect of ultrasonic impact treatment on surface stress evaluation of laser cladding coating by using critically refracted longitudinal wave

Residual Stress Inspection by Eu3+ Photoluminescence Piezo-Spectroscopy: an Application in Thermal Barrier Coatings

Study on the reduction of residual stress in laser cladding layers through groove texture

Measurement of two-dimensional residual stress in nanocrystalline superelastic NiTi fabricated with pre-strain laser shock peening

Residual Stress in Thermal Spray Coatings Measured by Curvature Based on 3d Digital Image Correlation Technique

Cross-Sectional Residual Stresses in Thermal Spray Coatings Measured by Moiré Interferometry and Nanoindentation Technique

Identifying residual stresses in laser welds by fatigue crack growth acceleration measurement

Numerical and experimental investigation into the evolution and distribution of residual stress in laser transmission welding of PC/Cu/PC

Optimization of Laser Glazing Parameters for Reduction of Residual-Stress

Non-contact Measurements of Residual Stress Distribution and Grain Size in Titanium Alloys with Laser Ultrasonic System

Residual Stress Measurement and Calibration for A7N01 Aluminum Alloy Welded Joints by Using Longitudinal Critically Refracted (LCR) Wave Transmission Method

Characterization of Elastic Modulus of Laser Cladding Coatings Using Laser Ultrasonic Method