Abstract:Because the compressor thin-blades of aero-engine often fractured in service, laser shock processing was suggested to be applied as a surface strengthening technology. Aim at the problem of compressive residual stress relaxation in laser-peened compressor thin-blades, TC11 titanium alloy thin-components were treated by laser shock processing and then conducted in axial tensile-tensile fatigue test and thermal insulation in vacuum. X-ray diffraction tests were carried out to obtain the relaxation rules of residual stress under fatigue loading and thermal stress loading. In addition, the relaxation mechanisms of residual stress were indicated. Experiment results demonstrate that surface compressive residual stress relaxes by 53%, and 95% of stress relaxation occurs in the previous 5 fatigue cycles under the fatigue loading (maximum stress sigma(max) = 500 MPa, stress ratio R=0.1). The surface relaxation degree and severely-relaxed depth increase with fatigue loading, and the relaxation mechanism is that plastic deformation of local area material results in residual stress redistribution. Surface compressive residual stress relaxes by 3%, 29% and 48% respectively after thermal insulation for 120 min under the constant temperature of 200 degrees C, 300 degrees C and 400 degrees C. Surface compressive residual stress relaxes by 18% and 58% respectively after thermal insulation for 120 min under the altering temperature of 200 degrees C + 400 degrees C and 300 degrees C + 400 degrees C. The relaxation all occurs in the previous 60 min. There is a similar trend with temperature in the aspect of severely-relaxed depth. The relaxation mechanism under thermal stress loading is that dislocations and grain-boundaries are activated to move and annihilated, and then plastic deformation recovery occurs. Due to the distinction of relaxation mechanisms, there is an obvious superimposed effect under the combined action of fatigue loading and thermal stress loading.

Optimization of Laser Glazing Parameters for Reduction of Residual-Stress

Structure Analysis of Laser Remelted Coating and Its Influential Factors

Residual Stress Analysis on the Ti-bioglass Coatings Produced by High Velocity Flame Spraying

Numerical Investigations on Residual Stress in Laser Penetration Welding Process of Ultrafine-Grained Steel

Optimization of Laser Repair Parameters for Precracked 304 Stainless Steel Components with Nanocomposites Addition

Process Optimization and Residual Stress Measurement for Arc Spraying Rapid Tooling

Study on the reduction of residual stress in laser cladding layers through groove texture

Optimization Of Residual Stresses Induced By Multiple Laser Shock Processing

Laser Remelting of Plasma-Sprayed Nanostructured Al2O3–20 Wt.% ZrO2 Coatings Onto 316L Stainless Steel

Process Optimization of laser remelting plasma -sprayed NiCr-Cr3 C2 coatings

Stepwise varying of laser parameters to enhance the residual stress field in multiple laser shock processing: numerical verification of single-point region

Temperature Field Numerical Calculation of Laser Re-melting HVOF Sprayed Cr3C2-25％ CrNi Coatings and Experiment Test

Effects of the Laser Micromelting Process Parameters on the Preparation of Micron-Sized FeCrAl Coatings on Zr Alloy Surfaces

Mechanism and Performance Characterization of Heat Treatment on Laser-Cladded Ni-WC Coatings

Simulation of the elasto-plastic response and residual stresses near metal surface due to laser shock processing

Study on Stability of Residual Stress Induced by Laser Shock Processing in Titanium Alloy Thin-Components

Modeling of the residual stresses in plasma-spraying functionally graded ZrO2/NiCoCrAlY coatings using finite element method

Quantitative analysis and experimental study of the influence of process parameters on the evolution of laser cladding

Numerical simulation of residual stress in SiC/316L composite coating by ultrasonic aided laser cladding

Residual Stress Control Using Process Optimization in Directed Energy Deposition

Investigation of Micro-Hardness, Wear Resistance, and Defects of 316L Stainless Steel and TiC Composite Coating Fabricated by Laser Engineered Net Shaping