Abstract:In this research, a novel method for fabricating flexible polyimide foams was developed. The foam was derived from the precursor synthesized via esterification of 3,3′,4,4′-oxydiphthalic anhydride and 4,4′-oxydianiline. After drying process, the remaining solvent acted as blowing agent. By adjusting the synthesis condition, low-molecular weight precursor was obtained and can be foamed under environment temperature. With this novel type of precursor and vacuum-assisted foaming process, we could easily obtain any shape of foams, which was easy to process under relatively low temperature. The foam could be imidized later in order to improve mechanical strength. During the imidization process, in situ Fourier transform infrared (FTIR) analysis was applied to analyze the variation of the imidization percentage with time. The density of the foams could be adjusted from 12 to 30 kg m−3 with uniform cell structure. Other properties of foams were also investigated. The glass transition temperature of the precursor was 70°C, which is obviously lower than that of the usual previously reported. The 5% and 10% weight loss temperatures of the finally imidized foam can reach up to 567°C and 593°C, respectively. The foams belong to open cell structure with 98% open cell content. The limiting oxygen index of the foams varied from 38.6 to 41.9, depending on foam densities. The compressive strength of the foam ranged from 30.6 to 90.6 kPa when the density changed from 15 to 28 kg m−3. In addition, the in situ FTIR analysis was applied to analyze the imidization percentage of the foam during imidization process.

STUDY ON THE SYNTHESIS AND PROPERTIES OF POLYIMIDE FOAMS

Studies on Polyimide Foams Prepared from Poly(Ester-amine Salt) Precursor Powder

Preparation and Property of Polyimide Foams

Preparation and Dielectric Properties of Polyimide Foams Containing Crosslinked Structures

Synthesis of poly(propylene glycol)-grafted polyimide precursors and preparation of nanoporous polyimides

Polyimide Foams with Ultralow Dielectric Constants

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

INFLUENCE OF THE CHEMISTRY OF THE FOAMING COMPOSITION ON THERMAL AND MECHANICAL PROPERTIES OF THE FORMING POLYIMIDE FOAM

A Novel Vacuum-Assisted Method for Fabricating Flexible Polyimide Foams from 3,3′,4,4′-Oxydiphthalic Anhydride/4,4′-Oxydianiline

Preparation and Properties of High-Temperature-Resistant, Lightweight, Flexible Polyimide Foams with Different Diamine Structures

Synthesis and Studies of Polyimide

Synthesis and Characterization of Polymer Nanofoams

Closed-Cell Rigid Polyimide Foams for High-Temperature Applications: The Effect of Structure on Combined Properties

Synthesis and Characterization of Biphenyl Polyimide Containing Alkyl Sulfide Structure

Preparation and Properties of Chopped Carbon Fiber Reinforced Polyimide Composite Foams

Study on Syntheses and Properties of Some Novel Polyimides Containing Bisthiazole Rings

Fabrication of rigid polyimide foams via thermal foaming of nadimide-end-capped polyester-amine precursor

Synthesis and Properties Study of Fluorinated Copolymer Polyimide

Preparation of Open-Cell Rigid Polyimide Foam via Nonaqueous High Internal Phase Emulsion-Templating Technique

Synthesis and Characterization of Polyimides Derived from 5-Amino-2(p-aminophenyl) Benzoxazole Monomer

Synthesis and characterization of fluorinated polyimides with high heat resistance and low dielectric constant