Abstract:Fan-out Wafer-level Packaging (FOWLP) urgently demands low dielectric constant and dissipation factor interlayer dielectric materials to mitigate high transmission loss at high frequencies. Polyimides (PIs) are widely used as interlayer dielectric materials in FOWLP for their excellent comprehensive properties. However, addressing the challenge of decreasing the dielectric constant and dissipation factor of PIs at high frequencies to meet the application requirements remains an active pursuit in both industry and academia. In this study, we designed and synthesized a novel diamine monomer featuring bis(trifluoromethyl) pendant groups, denoted as 4,4'-((3',5'-bis (trifluoromethyl)-[1,1'-biphenyl]-3,5-diyl)bis(oxy))dianiline (HFBODA). The binary polymerization of this diamine monomer with common dianhydrides led to promising outcomes. Remarkably, 6FDA-HFBODA exhibited excellent properties among the prepared PIs (Td,5% =521°C, Tg = 240°C, Dk = 2.63 and Df = 3.72×10-3 @ 10 GHz. Additionally, BPADA-HFBODA demonstrated an ultra-low Df value of 2.30×10-3 @ 10 GHz. The relationship between the charge density of imide in PIs and the dissipation factor of PIs was investigated for the first time. By introducing strong electron-withdrawing groups to the side group of PI, the effect of imide ring on orientation polarization was greatly declined, thus the dissipation factor of PI at high frequency was significantly decreased. Besides, the relationship between the structures and other essential properties of PIs in this study was systematically explored. This work provided a novel diamine and demonstrated the role of trifluoromethyl located in side group in lowering dissipation factors of PIs at high frequencies. The introduction of bis(trifluoromethyl) pendant group led to a reduction in polarizability and an increase in free volume within the PIs. Moreover, the electron-withdrawing effect of trifluoromethyl group substantially minimized the probability of internal friction among dipoles, resulting in reduced dielectric constants and dissipation factors. These findings provided crucial insights and guidance for the future design and research of low dielectric constant and dissipation factor PIs, particularly for high-frequency applications in Fan-out Wafer-level Packaging.

Polyimide Foams with Ultralow Dielectric Constants

Preparation and Dielectric Properties of Polyimide Foams Containing Crosslinked Structures

Preparation and Property of Polyimide Foams

Preparation of fluorinated poly(benzoxazole-co-imide) with low dielectric constants based on the thermal rearrangement reaction of o-hydroxy polyimides

Preparation and Properties of High-Temperature-Resistant, Lightweight, Flexible Polyimide Foams with Different Diamine Structures

Perfluorocyclobutyl-containing transparent polyimides with low dielectric constant and low dielectric loss

Poly(ester imide)s with Low Linear Coefficients of Thermal Expansion and Low Water Uptake (VII): A Strategy to Achieve Ultra-Low Dissipation Factors at 10 GHz

Synthesis and characterization of fluorinated polyimides with high heat resistance and low dielectric constant

Synthesis and Characterization of High Fluorine‐containing Polyimides with Low‐dielectric Constant

Fabrication of Lightweight Polyimide Foams with Exceptional Mechanical and Thermal Properties

Thermoplastic Polyimide with Low Dielectric Properties Enabled by the 2,2′-Spirobifluorene Group

Preparation of fluorinated polyimides with low dielectric constants and low dielectric losses by combining ester groups and triphenyl pyridine structures

Low Dielectric Post-Cured Benzocyclobutene-Functionalized Fluorine-Containing Polyimide Material

Polyimides with Low Dielectric Constant and Dissipation Factor at High Frequency Derived from Novel Aromatic Diamine with Bistrifluoromethyl Pendant Groups

Polyimide Films Based on β-Cyclodextrin Polyrotaxane with Low Dielectric and Excellent Comprehensive Performance

Preparation of Polyimide Films with Ultra-Low Dielectric Constant by Phase Inversion

Reducing the Permittivity of Polyimides for Better Use in Communication Devices

Organosoluble polyimides with low dielectric constant prepared from an asymmetric diamine containing bulky m-trifluoromethyl phenyl group

Fabrication of multifunctional polyimide foams with co-polymerized benzimidazole moieties for excellent thermal insulation and flame retardancy applications

Frequency-dependent dielectric properties of aromatic polyimides in the 25–330 GHz range

Porous polyimide composite films containing mesoporous hollow silica nanospheres with ultralow dielectric constant and dissipation loss