Abstract:In this work, the mechanical mixing process was successfully used to inoculate FeCrNiMnAl powder with CeO 2 nanoparticles, which contributed to the heterogeneous nucleation of fine equiaxed grains. In this way, the nano-CeO 2 /FeCrNiMnAl HEA composite coating with low dilution, cracks-free was successfully fabricated. The effects of different addition of nano-CeO 2 (0 wt%, 0.5 wt%, 1.0 wt%, 1.5 wt%, 2.0 wt%) on the microstructure and properties of HEA composite coatings were mainly explored. The thermodynamic calculations on HEA composite coatings with different contents of CeO 2 were conducted to predicted their phase composition. With the modification of nano-CeO 2 , the microstructure exhibited homogenous, fine-grained and equiaxed. To further reveal the effect of CeO 2 on the microstructure, this work studied the columnar-to-equiaxed transition (CET) behavior of HEA coating during solidification process. As a comparison, the heterogeneous nucleation behavior of fine equiaxed grains induced by nano-CeO 2 in HEA composite coatings was studies. The results showed that CeO 2 nanoparticles were enriched at the grain boundaries of HEA composite coating, and it not only had a drag effect, but also hindered the growth and development of grains. However, excessive nano-CeO 2 (2.0 wt% CeO 2 ) could affect the forming quality of HEA coating and have a negative impact on the mechanical properties. After regulating the grain structure, the mechanical properties of HEA composite coating have been greatly improved. While 1.0 wt% nano-CeO 2 was added, the microhardness of HEA composite coating reached to the maximum (670.4 HV 0.2 ). Compared with substrate, the average microhardness has increased almost 91.5 %. The friction performance of 1.0 wt% CeO 2 /FeCrNiMnAl HEA composite coating was the optimal as well and the wear rate reached 3.12 × 10 −6 mm 3 /N m. The tribo-oxide layer was produced on the worn surface of HEA composite coating.

Preparation and Characterizations of Fe/Ce Oxidation Nano Glass Coatings

Preparation of multilayer coated glass with low-E and thermal insulation properties

A Triple-layer Glass-coating for Low Emissivity and Photocatalytic Activity

Optical properties of glass coatings containing Fe and Co

Effect of Mass Fraction of CeO2 on Leaching Resistance of Sodium Aluminosilicate Glass

Enhancing oxygen‐blocking properties of HfB2‐MoSi2‐SiC coating by CeO2 modification

Preparation of TiOx-C Nano-Composite Films as Solar Selective Absorbers by Sol-Gel Method

Highly Enhanced Infrared Spectral Emissivity of Porous CeO2 Coating

Effect of (Fe0.8Cr0.2)2O3 pigment on the optical properties of ZnO–B2O3–SiO2 glass-based coatings for double-glass photovoltaic modules

Sol-Gel auto-combustion, structural, photo-catalytic activity and UV-VIS study of Co1-xZnxFe2-yCeyO4 NPs (x = 0.3, y = 0.04)

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

Preparation and Modification of Nano-Zno/ceo2 Composite Oxides

A correlative effect of Fe3+ ion incorporation on the structure-optic and photocatalytic properties of CeO2 nanoparticles

Electrocatalytic and antifouling properties of CeO2-glassy carbon electrodes

Synthesis, Characterization of Ceo2@Zif-8 Composite Abrasives and Their Chemical Mechanical Polishing Behavior on Glass Substrate

Effect of nano-sized CeF3 on microstructure, mechanical, high temperature friction and corrosion behavior of Ni–W composite coatings

Preparation of Α- Fe_2O_3 - TiO_2 on Glass Substrates and Its Photo-Catalyst Properties

Preparation of Nanometer Cerium Oxide by Microwave Irradiation and Study on Its Surface Modification

Preparation and Characterization of Ceria-Zirconia Ceramics Using a Sol-Gel Process

A novel approach to regulate the microstructure of laser-clad FeCrNiMnAl high entropy alloy via CeO 2 nanoparticles

Tuning the UV absorbing ability of CeO2 nanoparticles with F− doping