A Triple-layer Glass-coating for Low Emissivity and Photocatalytic Activity

Han Gao-rong

2008-01-01

Abstract:A triple-layer composite film of SiC_xO_y/SnO_2:F/TiO_2,which combines low-emissivity(low-e) property and photocatalytic activity for the glasscoating,was fabricated.The layer of SiC_xO_y is deposited directly on glass substrate,acting as the barrier layer to prevent the ions diffusion from glass substrates to outside layers.The functional layers of SnO_2:F and TiO_2 devote to low-e and photocatalytic activity properties for the composite film,respectively. Measurements were performed by X-ray Diffraction(XRD),Scanning Electron Microscopy(SEM) and Fourier Transform Infrared(FTIR) spectrophotometer.Compared to the pure TiO_2 film,the composite film shows higher photocatalytic and hydrophilic activities,which might be due to the rugged surface and the interfacial electron transfer from TiO_2 layer to SnO_2 layer.On the other hand,the reflectance of composite films in far-range infrared region,which is due to the low-E property of SnO_2:F layer,decreases with the increasing of TiO_2 film thickness.