Abstract:Nano-crystal TiO2 Sol was prepared by sol-gel technique with tetrabutyl titanate as precursor. The aggregation of nano-TiO2 particles can be effectively suppressed by adding acrylic acid as surface modifier in the solution. Polyethylene glycol (PEG) with different relative molecular mass (1540, 6 000, 10 000, 20 000) was used in preparation of nano-TiO2 thin films, and the nano-TiO2 thin films with micro-pore structure were obtained by adding PEG as dispersing agent. Furthermore, the porosity increases with the increase of relative molecular mass of PEG. The analysis of DTA-TG indicated that the volatilizing temperature of water and solvent in the samples is about 57 degreesC, and that the decomposition and combustion temperatures of the organics in the sample are 213 degreesC and 220similar to350 degreesC respectively. XRD patterns of the samples annealed at different temperatures demonstrated that the phase transform temperature is ca 700 degreesC and the aggregation of nano-TiO2 is obviously appeared at this temperature. The proper thermotreatment temperature for nano-TiO2 as prepared is ca 600 degreesC. The photocatalytic activity of nano-TiO2 porous thin films and TiO2 powder catalyst for degradation of X-3B was investigated. The experimental results indicated that the two kinds of photocatalysts, especially powder photocatalyst, have high photocatalytic activity in photocatalytic degradation of X-3B. Moreover, the photocatalytic activity of nano-TiO2 thin films with PEG is higher than that of the film without PEG.

Preparation of TiOx-C Nano-Composite Films as Solar Selective Absorbers by Sol-Gel Method

A facile process to prepare crosslinked nano-graphites uniformly dispersed in titanium oxide films as solar selective absorbers

Porous Carbon–titania Nanocomposite Films for Spectrally Solar Selective Absorbers

Controllable Fabrication and Characterization of Porous C/TiO2 Nanocomposite Films As Solar Selective Absorber

Preparation and characterization of porous carbon–titania nanocomposite films as solar selective absorbers

Structure and optical properties of carbon–TiO 2 composite thin films by sol–gel method as solar selective absorbers

Structure and Optical Properties of Carbon–tio2 Composite Thin Films by Sol–gel Method As Solar Selective Absorbers

Preparation and photothermal conversion performance of carbon-silica nanocomposite films for spectrally selective solar absorbers

The Preparation of TiO_(2-x)N_x(0<x<1) Thin Films by Sol-Gel Method and Its Photocatalysis and Hydrophilic Properties

A One-Step Method to Prepare Carbon and Dielectric Composited Films Featuring a Skeleton–skin Structure

Study of Self-Cleaning and Low-Emission Properties of FTO/TiO2 Composite films

Carbonaceous Nickel Oxide Composite Films with Homogenously Dispersed Metallic Ni Nanoparticles by a Facile Sol–gel Method

The Preparation of TiO_2 Nano-film by Sol-Gel and Its Properties

Control of optical properties of TiN x O y films and application for high performance solar selective absorbing coatings

Preparation of Nano-crystal TiO2 Porous Thin Films and Their Photocatalytic Performance

Preparation and Characterization of TiO2/ZnO Nano Composite Film Via Sol-Gel Process

Study on the Preparation of TiO_2 Nano Film Via Sol-Gel Process

Microstructure, optical and optoelectrical properties of mesoporous nc-TiO2 films by hydrolysis-limited sol–gel process with different inhibitors

The Preparation and Characterization Of Nanostructure TiO2 Thin Films and TiO2 Porous Thin Films By Sol-Gel Method

Preparation and Bioactivity Study of TiO2 Nanotubes/Mesoporous SiO2 Composite Films

Preparation and Photocatalytic Study of TiO; Nano Composite Film