Abstract:In this study, four kinds of heat treatments were performed to obtain a certain amount of retained austenite, which can result in good toughness and low brittleness accompanied with wear resistance of an in situ VC particle reinforced iron-based composite (VCFC). Microstructure, mechanical properties and wear resistance of the samples under heat treatment of QP, QPT, MQP and MQPT were compared. The experimental results indicated that there is a huge difference in microstructure between MQPT and the other heat treatments. High-proportion retained austenite and white net-like precipitates of M7C3 carbide existed in the MQPT-treated sample, but thick M7C3 carbide with brittleness was discovered in the other sample. Thereby, high-proportion retained austenite contributed to its low hardness of 634 HV and high tensile strength of 267 MPa, while a maximum hardness of 705.5 HV and a minimum tensile strength of 205 MPa were exhibited in the QPT-treated sample with a V-rich carbide of high hardness, a Cr-rich carbide of brittleness and a high-proportion martensite. Meanwhile, a phase transformation from retained austenite to martensite could increase the hardness and enhance wear resistance based on the transformation-induced plasticity (TRIP) effect; its wear rate was only 1.83 × 10−6 mm−3/(N·m). However, the wear rates of the samples under QP, QPT and MQP heat treatments increased by 16.4%, 44.3% and 41.0%, respectively. The wear mechanism was a synergistic effect of the adhesive wear mechanism and the abrasive wear mechanism. The adhesive wear mechanism was mainly considered in the MQPT-treated sample to reduce the wear rate attributed to high-proportion retained austenite and the existence of wear debris with a W element on the surface of the wear track. However, the abrasive wear mechanism could exist in the other samples because of a lot of thick, brittle M7C3, thereby resulting in a higher wear rate due to immediate contact between the designed material and the counterpart.

Microstructure and Wear Resistance of Iron Matrix Composites Reinforced by In-Situ Carbides

Interfacial bonding and wear behavior of macroscopic TiC particulates reinforced iron-based composites fabricated by infiltration casting process

Microstructural evolution and performance analysis of WC-11Co reinforced iron matrix composites

Interfacial Bonding And Abrasive Wear Behavior Of Iron Matrix Composite Reinforced By Ceramic Particles

Influence of Tungsten on Microstructure and Properties of As-Cast Hi-Cr Cast Iron

Microstructure and high-temperature wear properties of in situ TiC composite coatings by plasma transferred arc surface alloying on gray cast iron

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

In-situ Production and Microstructure of TiC/Fe_3Al Composites

Interface microstructure and abrasive wear properties of WC-iron matrix composites with Ni, Mo, Fe added to the preforms

Microscopic Study of Carbide Precipitation during Heat Treatment of 35Cr–4C High Chromium Cast Iron

Effect of In-Situ (ti&w)c Multiphase Particles on Three-Body Abrasive Wear of High Chromium Cast Iron

Preparation and Microstructural Characterization of a High-Cr White Cast Iron Reinforced with WC Particles

Recent Developments in Fabrication of Ceramic Particle Reinforced Iron Matrix Wear Resistant Surface Composite Using Infiltration Casting Technology

Microstructure evolution, mechanical properties, and wear behavior of in-situ TiCx/TC4 composites

Investigating Microstructural Evolution and Its Influence on Tribological Behaviors of In-Situ Formed VCp Reinforced Iron-Based Composites with Variable Mn Content

The Correlation Analysis of Microstructure and Tribological Characteristics of In Situ VCp Reinforced Iron-Based Composite

On the Preparation and Wear Properties of Ceramic Particle-reinforced High-chromium Cast Iron-based Surface Composite Material

Effect of the amount of SiC particles on the microstructure, mechanical and wear properties of FeMnCoCr high entropy alloy composites

Microstructures and mechanical properties of in-situ FeCrNiCu high entropy alloy matrix composites reinforced with NbC particles

Spark Plasma Sintering Preparation of Tungsten Carbide-Reinforced Iron-Based Composite Materials: Wear Resistance Performance and Mechanism

Preparation and Properties of ZTA + WC Particles/Hypereutectic High Chromium Cast Iron Composites