Abstract:In this study, red mud was used as the main raw material to prepare polyaluminum-ferric chloride (PCFA) with high added value. The effects of the liquid–solid ratio, reaction temperature, reaction time, hydrochloric acid concentration during acid leaching, polymerization time, OH − /Fe molar ratio, and polymerization temperature on the preparation of PCFA were investigated and determined by conducting single-factor optimization experiments under optimal preparation conditions. Characterization results show that the surface of the PCFA flocculant has compact and dense porosity and a dense sheet-like structure, and PCFA contains hydroxyl-bridged iron–aluminum polymers. When the settling time was 30 min, the stirring intensity was 200 rpm; the initial concentration of Nano-titanium dioxide(TiO 2 -NPs) was 30 mg·L −1 ; the pH value was 7.0; the dosage of PCFA was 25 mg·L −1 , and the optimum removal rates of TiO 2 -NPs and turbidity were 84.8% and 81.3%, respectively. The flocs produced by PCFA treatment of TiO 2 -NPs were large and dense. Under optimal flocculation conditions, the average particle size of PCFA-TiO 2 -NP flocs was 2.98 μm, and the fractal dimension was 1.66. Based on the abovementioned flocculation experimental data, a Grey correlation method was established to evaluate the degree of correlation among factors such as ionic strength, settling time, stirring strength, kaolin concentration, initial concentration, reaction pH value, and dosage and the performance of PCFA coagulation to remove TiO 2 -NP-containing wastewater. In the reaction system of the PCFA coagulation of TiO 2 -NPs, the dosage is the most important factor.

Preparation of Composite Inorganic Polymer Coagulant of Polymeric Aluminum Ferric Chloride Reusing Kaolin Tailings

Preparation and Application of Slag Compound Flocculant

Coagulation performance and mechanism of polyaluminum ferric chloride (PAFC) coagulant synthesized using blast furnace dust

Novel Polyaluminum Ferric Chloride Composite Coagulant from Bayer Red Mud for Wastewater Treatment

Preparation of polymeric aluminum ferric chloride and its application in advance treatment of coking wastewater

Preparation of inorganic-organic composite coagulants PAFC-PDA and its effects on treating synthetic printing and dyeing wastewater

Preparation of a Composite Coagulant: Polymeric Aluminum Ferric Sulfate (PAFS) for Wastewater Treatment

Red Mud-Based Polyaluminum Ferric Chloride Flocculant: Preparation, Characterization and Flocculation Performance

Composite Flocculants Prepared by Waste Aluminum

Preparation and applications of inorganic polymer composite flocculant poly aluminum ferric sulfate

Flocculation Performance of PCFA Composite Coagulant for Removing Nanoparticles

Preparation and Applications of Inorganic Polymer Flocculant Poly Aluminum Ferric Sulfate

Optimization of Preparation and Application of Polymeric Aluminum Ferric Sulfate Coagulant by Response Surface Analysis

Production of Polyaluminum Ferric Chloride from Blast Furnace Dust

Red Mud-Based Polyaluminium Ferric Chloride Flocculant: Preparation, Characterisation, and Flocculation Performance

PREPARATION AND APPLICATION OF POLYMER FERRIC ALUMINUM SULFATE CHLORIDE FLOCCULANT

Characterization and coagulation–flocculation behavior of polymeric aluminum ferric sulfate (PAFS)

Preparation and Application of Polyaluminum Ferric Sulfate from Red Mud: Behaviors of Leaching, Polymerizing, and Coagulation

Study on the pretreatment of printing & dyeing wastewater with composite polyaluminum ferric flocculants

High-efficiency leaching of Al and Fe from fly ash for preparation of polymeric aluminum ferric chloride sulfate coagulant for wastewater treatment

Study on the preparation of polysilicate ferric flocculant and its treatment of high turbidity tailings water